采用粘结相成分设计方法制备了一种新型自锐化钨合金材料,对所获得的材料进行了微观分析和性能测试.结果表明:与相同钨含量的常规钨合金相比,所制备的新型钨合金材料的动态抗压缩强度很高;在动态压缩加载条件下,材料的破坏形式为沿着试样加载方向(轴向)发生劈裂脱落,基本不出现塑性变形行为,这种特殊的失效模式有利于弹体在侵彻过程中产生"自锐化"现象.
参考文献
| [1] | 程兴旺,王富耻,王鲁,李树奎.垂直侵彻钢靶过程中钨合金壳体破坏机理研究[J].稀有金属材料与工程,2002(06):427-431. |
| [2] | Magness L S .[J].Mechanics of Materials,1994,17(02):147. |
| [3] | Magness L S;Kapoor D;Dowding R J .[J].Materials and Manufacturing Processes,1995,10(03):531. |
| [4] | Gerlach U .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1986,17A(03):435. |
| [5] | Dunn P S.Damkroger[A].New Jersey:Metal Powder Industries Federation,1995:199. |
| [6] | Kecskesa L;Hall I W .[J].Journal of Materials Processing Technology,2001,94(2-3):247. |
| [7] | Yadav S;Ramesh K T .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,1995,A203(1-2):140. |
| [8] | Belhadjhamida A;German R M.[A].New Jersey:Metal Powder Industries Federation,1993:195. |
| [9] | Griffo A .Processing and Physical Metallurgy of Tungsten -Nickel Aluminide Composites[D].Pennsylvania:The Pennsy lvania State University,1996. |
| [10] | Bose A;Rabin B H;German R M .[J].Metal Powder Report,1987,42(12):834. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%