为了保证自密实轻骨料混凝土(Self-compacting lightweight concrete,SCLC)在实际工程中的安全运用,本文分别对强度为C40和C50的自密实轻骨料混凝土试件进行了高温爆裂试验.通过测定混凝土试验前后的质量、超声波速、抗压强度和抗折强度,研究了自密实轻骨料混凝土的高温性能,并和同强度的普通混凝土、轻骨料混凝土和自密实混凝土的高温性能进行了对比.结果表明,自密实轻骨料混凝土比普通混凝土易爆裂,质量损失较大,但是高温后的超声波速和残余强度损失均小于普通混凝土.
参考文献
| [1] | Caijun Shi;Yanzhong Wu .Mixture Proportioning and Properties of Self-Consolidating Lightweight Concrete Containing Glass Powder[J].ACI materials journal,2005(5):355-363. |
| [2] | Chao-Lung Hwang;Meng-Feng Hung .Durability design and performance of self-consolidating lightweight concrete[J].Construction and Building Materials,2005(8):619-626. |
| [3] | Zhimin Wu;Yunguo Zhang;Jianjun Zheng;Yining Ding .An Experimental Study On The Workability Of Self-compacting Lightweight Concrete[J].Construction and Building Materials,2009(5):2087-2092. |
| [4] | Jacek Kwasny;Mohammed Sonebi;Susan E. Taylor;Yun Bai;Kieran Owens;William Doherty .Influence of the Type of Coarse Lightweight Aggregate on Properties of Semilightweight Self-Consolidating Concrete[J].Journal of Materials in Civil Engineering,2012(12):1474-1483. |
| [5] | Jean-Christophe Mindeguia;Pierre Pimienta;Albert Noumowe .Temperature, pore pressure and mass variation of concrete subjected to high temperature — Experimental and numerical discussion on spalling risk[J].Cement and Concrete Research,2010(3):477-487. |
| [6] | Hsuanchih Yang;Yiching Lin;Chiamen Hsiao;Jian-You Liu .Evaluating Residual Compressive Strength Of Concrete At Elevated Temperatures Using Ultrasonic Pulse Velocity[J].Fire safety journal: An international journal devoted to research on fire safety science and engineering,2009(1):121-130. |
| [7] | Khoury G A .Compressive strength of concrete at high temperatures:a reassessment[J].magazine of concrete research,1992,44(161):291-309. |
| [8] | Copier W J .The spalling of normalweight and lightweight concrete on exposure to fire[J].Heron,1979,24(02):1-92. |
| [9] | B. Persson .Fire resistance of self-compacting concrete, SCC[J].Materials and structures,2004(273):575-584. |
| [10] | A. Noumowe;H. Carre;A. Daoud;H. Toutanji .High-Strength Self-Compacting Concrete Exposed to Fire Test[J].Journal of Materials in Civil Engineering,2006(6):754-758. |
| [11] | Hans W. Reinhardt;Michael Stegmaier .Self-Consolidating Concrete in Fire[J].ACI materials journal,2006(2):130-135. |
| [12] | Kosmas K. Sideris .Mechanical Characteristics of Self-Consolidating Concretes Exposed to Elevated Temperatures[J].Journal of Materials in Civil Engineering,2007(8):648-654. |
| [13] | Jin Tao;Yong Yuan;Luc Taerwe .Compressive Strength of Self-Compacting Concrete during High-Temperature Exposure[J].Journal of Materials in Civil Engineering,2010(10):1005-1011. |
| [14] | D. Rama Seshu;A. Pratusha .Study on compressive strength behaviour of normal concrete and self-compacting concrete subjected to elevated temperatures[J].Magazine of concrete research,2013(7/8):415-421. |
| [15] | Harun Tanyildizi;Ahmet Coskun .Performance of lightweight concrete with silica fume after high temperature[J].Construction and Building Materials,2008(10):2124-2129. |
| [16] | 孙庆霞 .纤维增强陶粒混凝土耐高温性能的实验研究[D].兰州理工大学,2009. |
| [17] | Noumow é A;Siddique R;Ranc G .Thermo-mechanical characteristics of concrete at elevated temperatures up to 310℃[J].Nudesr Engineering and Design,2009,239(03):470-476. |
| [18] | Castillo C;Durrani A J .Effect of transient high temperature on high-strength concrete[J].ACI Materials Journal,1990,87(01):47-53. |
| [19] | Matesová D;Bonen D;Shah S .Factors affeeting theresistance of cementitious materials at high temperatures and medium heating rates[J].Materials and Structures,2006,39(09):919-935. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%