Microstructure, precipitates and fracture morphology in the weld metal and the heat-affected zone (HAZ) of Cr18Mo2 ferritic stainless steel have been studied by means of metalloscope, SEM,TEM and X-ray diffractometer. Experimental results indicate that crystalline grain coarsening in HAZ is one of the reason resulting in the embrittlement fracture in the welding zone of the ferritic stainless steel. Some precipitates (TiC, TiN and Cr2N) in the steel promote production and development of the brittle cracks. In practical applications. the welding heat input should be as small as possible to prevent embrittlement caused by HAZ grain coarsening.