为了提高热轧盘条的表面耐腐蚀性,使盘条在运输存放过程中不易腐蚀生锈,采用了红外光谱、扫描电镜、电化学方法及加速腐蚀试验对高、中、低碳钢热轧盘条的氧化皮试样进行了分析,研究了热轧盘条氧化皮的厚度、致密性以及与基体的结合性对基体保护的规律.结果表明:氧化皮厚度均匀,致密性好,与基体结合好的都能提高防腐蚀性能.
参考文献
| [1] | 魏宝明.金属腐蚀理论及应用[M].北京:化学工业出版社,2004:10-20. |
| [2] | 李铁藩.金属高温氧化和热腐蚀[M].北京:化学工业出版社,2003:3-6,51-54,168-172. |
| [3] | 陈惠玲,魏雨.碳钢在含SO2环境大气中腐蚀机理的研究[J].腐蚀与防护,2006(06):284-286. |
| [4] | 杨晓梅.大气腐蚀研究中钢锈层的光谱分析[J].光谱学与光谱分析,2000(03):347-349. |
| [5] | T. Nishimura .Rust formation and corrosion performance of Si- and Al-bearing ultrafine grained weathering steel[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(5):1306-1312. |
| [6] | M.F. Frolish;M. Krzyzanowski;W.M. Rainforth .Oxide scale behaviour on aluminium and steel under hot working conditions[J].Journal of Materials Processing Technology,2006(1/3):36-40. |
| [7] | 王银军,董汉君,穆海玲,陈家光.卷取后的热轧带钢氧化铁皮显微分析[J].中国冶金,2007(10):40-44. |
| [8] | A. Chattopadhyay;N. Bandyopadyay;A. K. Das .Oxide Scale Characterization of Hot Rolled Coils by Raman Spectroscopy Technique[J].Scripta materialia,2005(3):211-215. |
| [9] | Krzyzanowski M.;Beynon JH. .Modelling the boundary conditions for thermo-mechanical processing - oxide scale behaviour and composition effects[J].Modelling and simulation in materials science and engineering,2000(6):927-945. |
| [10] | Krzyzanowski M;Beynon J H;Sellars C M .Analysis of secondary oxide scale failure at entry into the roll gap[J].Metallic Material Transaction,2000,31 B:1 483-11490. |
| [11] | 中村;王怀宇 .板坯加热时氧化铁皮的高温剥离性[J].宽厚板,1997,3(06):42-46. |
| [12] | 何建新,秦晓洲,易平,杨德模,李泽华,赖丽勤.Q235钢海洋大气腐蚀暴露试验研究[J].表面技术,2006(04):21-23. |
| [13] | M. Krzyzanowski;J. H. Beynon .Measurement of oxide properties for numerical evaluation of their failure under hot rolling conditions[J].Journal of Materials Processing Technology,2002(0):398-404. |
| [14] | 程英亮,吴海兰,李玲玲,陈振华,王慧敏,张昭,吴有伍.ZK60镁合金磷酸盐及锡酸盐化学转化膜[J].中国有色金属学报,2007(05):676-682. |
| [15] | 林方婷,石旺舟,马学鸣.冷却速率对低碳钢线材表面氧化皮微观结构的影响[J].华东师范大学学报（自然科学版）,2006(04):23-28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%