以有机硅改性丙烯酸环氧单酯为树脂配制了一系列紫外光-热混杂固化体系,用红外光谱(FT-IR)表征了固化过程特征吸收峰的变化；测试了有机硅链段的长短对固化膜表面水接触角、表面能和硅元素分布的影响.结果表明,在相同稀释剂条件下,丙烯酸环氧单酯光-热固化膜的表面水接触角为62.53°,表面能为47.62 mN/m,有机硅改性丙烯酸环氧单酯体系光-热固化膜的表面水接触角最高可达106.75°,相应的表面能为18.62 mN/m.有机硅改性体系中随着有机硅链段的增长,固化膜表面水接触角和表面硅元素含量逐渐增加,表面能则逐渐下降,表面元素分析也显示固化膜表面硅元素含量要比背面的高.
参考文献
| [1] | Marco Sangermano;Monica Cerrone;Giovanna Colucci .Preparation and characterization of hybrid thiol-ene/epoxy UV-thermal dual-cured systems[J].Polymer international,2010(8):1046-1051. |
| [2] | Young-Jun Park;Dong-Hyuk Lim;Hyun-Joong Kim .UV- and thermal-curing behaviors of dual-curable adhesives based on epoxy acrylate oligomers[J].International Journal of Adhesion & Adhesives,2009(7):710-717. |
| [3] | Simic S;Dunjic B;Tasic S;Bozic B;Jovanovic D;Popovic I .Synthesis and characterization of interpenetrating polymer networks with hyperbranched polymers through thermal-UV dual curing[J].Progress in Organic Coatings: An International Review Journal,2008(1):43-48. |
| [4] | Yuan HY;Lu XY;Zeng ZH;Yang JW;Chen YL .Allyl ether-modified unsaturated polyesters for UV/air dual-curable coatings. I: Synthesis and characterization of the oligomers and their cured films[J].Journal of Applied Polymer Science,2004(5):2765-2770. |
| [5] | 刘红波,余林梁,陈鸣才,何涛,王志霞.丙烯酸环氧单酯的合成及光-热固化性能[J].高分子材料科学与工程,2005(02):121-124. |
| [6] | 刘红波,张武英,林峰,何涛.聚氨酯改性丙烯酸环氧单酯的光-热固化性能[J].辐射研究与辐射工艺学报,2011(05):275-279. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%