采用光学显微镜研究了固溶和时效处理对0Cr21Ni6Mn9N含氮奥氏体不锈钢显微组织的影响.结果表明:0Cr21Ni6Mn9N钢冷拔管经1 100℃固溶处理后,晶粒尺寸变大,孪晶数量增多且层厚增加,晶界及晶粒均很清晰,无任何析出物;经固溶及650℃时效处理后,晶粒尺寸与固溶态的相差不大,但晶界上有大量黑色粒状M23C6相析出;经固溶及850℃时效处理后,出现大晶粒吞并小晶粒的现象,晶粒发生了二次长大,且晶界处的M23C6相数量较650℃时效的有所减少.
参考文献
| [1] | 刘树勋,刘宪民,刘蕤,王春旭,邢峰.0Cr21Ni6Mn9N奥氏体不锈钢的应变强化行为[J].钢铁研究学报,2005(04):40-44. |
| [2] | Chang, Y.H.;Luo, C.;Chen, C.A.;Chen, S.X..Effect of deuterium pre-charging on the mechanical properties, phase and deformation texture of 21-6-9 austenitic stainless steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2013:23-28. |
| [3] | M. E. Kassner;P. Geantil .Yield Stress of 21-6-9 Stainless Steel Over Very Wide Ranges of Strain Rates and Temperatures[J].Journal of Materials Engineering and Performance,2012(1):69-73. |
| [4] | 杨亮,董建新,何智勇,张麦仓.690合金管冷轧及退火处理过程中的组织演变[J].材料热处理学报,2011(12):98-104. |
| [5] | 杨钢,孙利军,张丽娜,王立民,王昌.形变孪晶的消失与退火孪晶的形成机制[J].钢铁研究学报,2009(02):39-43. |
| [6] | 李华英,丁桦,蔡志辉,吴志强,邱春林,黄明丽.固溶处理对Fe-25Mn-1Al-0.2C钢组织性能的影响[J].材料热处理学报,2012(09):70-74. |
| [7] | 黄西成,陈裕泽,陈勇梅,牛伟.2169钢细观损伤参数识别[J].材料工程,2007(04):50-52. |
| [8] | 代永娟,米振莉,唐荻,吕建崇.退火温度对Fe-Mn-TWIP钢微观结构的影响[J].材料热处理学报,2011(03):115-119. |
| [9] | 水恒勇,刘继雄,李美琳,赵爱民,曹嘉丽.热处理工艺对新型节镍奥氏体无磁钢组织和性能的影响[J].机械工程材料,2012(05):69-72. |
| [10] | 刘小勇,程世长,高家诚,包汉生,刘正东.新型12%Cr耐热钢650℃长时时效后的组织和高温强度[J].机械工程材料,2011(03):56-59. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%