采用接枝共聚的方法,即环氧和丙烯酸反应,环氧开环的同时生成带有羟基的丙烯酸单体,加入引发剂结合另外2种丙烯酸单体,在催化剂的作用下接入有机硅,制得有机硅环氧丙烯酸树脂.讨论了环氧树脂的用量对涂膜性能的影响、涂料的水解特性,并进行了实海挂板实验.结果表明:当环氧的用量为10％时,制备的防污涂料与水的接触角达到133°,附着力1级；有机硅/环氧改性丙烯酸树脂制得的防污涂料在海水中能够稳定地水解,兼具低表面能和自抛光的特性,实海挂板实验结果表明,涂料具有良好的防污性能.
参考文献
| [1] | Kumar SA;Balakrishnan T;Alagar A;Denchev Z .Development and characterization of silicone/phosphorus modified epoxy materials and their application as anticorrosion and antifouling coatings[J].Progress in Organic Coatings: An International Review Journal,2006(3):207-217. |
| [2] | ANANDA S;SANKARA T .Thermal properties of siliconized epoxy interpenetrating coatings[J].Progress in Organic Coatings,2002,45(03):323-326. |
| [3] | Yebra DM;Kiil S;Dam-Johansen K .Antifouling technology - past, present and future steps towards efficient and environmentally friendly antifouling coatings[J].Progress in Organic Coatings: An International Review Journal,2004(2):75-104. |
| [4] | 彭志强,谢晓君,张东亚,谢天禄.无锡自抛光防污涂料的研制[J].上海涂料,2004(04):7-9. |
| [5] | 孙博,邱星林.船舶防污涂料的研究现状及进展[J].广州化工,2008(03):13-16. |
| [6] | 钱斯文,董树华,刘勇,吴文健.低表面能涂料防污性能评价的快速试验方法[J].新技术新工艺,2008(08):66-69. |
| [7] | 陈美玲,曲园园,杨莉,高宏.SiO2改性低表面能纳米结构无毒海洋防污涂料[J].化工新型材料,2008(05):71-72. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%