在面内纯剪切载荷作用下，采用试验与有限元模拟方法研究了结构中心设置椭圆形大开口的正方形复合材料层合板的应力／应变集中现象及屈曲、后屈曲行为，通过测试结果对试验件失效模式进行了评估。研究结果表明：层合板开口附近应力／应变集中程度很高；大尺寸开口使结构稳定性显著降低，且开口层合板具有较好的后屈曲承载能力；由于弯曲产生高水平的层间应力，导致局部分层损伤并伴有基纤剪切破坏；随着横向挠度的增加，各应力集中区域的纤维发生拉伸断裂，导致整体结构瞬间发生脆性失效。有限元模拟结果与试验结果符合较好。
Experiments and finite-element-method(FEM) analysis have been conducted to investigate the effect of a large size elliptical cutout on the stress/strain concentration and buckling, post-buckling behaviour of a square composite laminate under in-plane shear load. It is observed that the stress/strain coneentration near the vicinity of cutout is considerable and the stability of the laminate declines remarkably due to the large cutout. The post- buckling loading capacity of laminate structure with a cutout is specific high. The failure modes of the test panel evaluated by experiments show that the high inter-laminar stress induced by the bending of laminate leads to the local damage of delamination companied by the fibre matrix shear- out, And with the structure's horizontal deflection increasing, the fibre in the stress/strain concentration area is stretched to fracture resulting in the whole laminate collapsed instantaneously. The FEM an~lvsis r 1. 11 ...:.L .L_
参考文献
| [1] | 杨乃宾,章怡宁.复合材料飞机结构设计[M].沈阳:航空工业出版社,2002: 114-118. |
| [2] | Ghannadpour SAM, Najafi A, Mohammadi B. On thebuckling behavior of cross-ply laminated composite plates dueto circular/elliptical cutouts [J]. Composite Structures. 2006,75: 3-6. |
| [3] | Jain P, Kumar A. Postbuckling response of square laminateswith a central circular/elliptical cutout [ J ]. CompositeStructures, 2004. 65(2) : 179-185. |
| [4] | Komur M A, Sen F,Atas A, et al. Buckling analysis oflaminated composite plates with an elliptical/circular cutoutusing FEM [J]. Advances in Engineering Software * 2010,41(2): 161-164. |
| [5] | Komur M A,Sonmez M. Elastic buckling of rectangular platesunder linearly varying in - plane normal load with a circularcutout [ J ]. Mechanics Research Communications, 2008,35(6): 361-371. |
| [6] | Oabay M, Ozer D. The analysis of elasto - plastic stresses inthe composite laminate with a circular hole subjected toin-plane loads by means of finite element method [J]. Journalof Reinforced Plastics and Composites, 2005,24(6) : 621-631. |
| [7] | Singh S B,Kumar A. Postbuckling response and failure ofsymmetric laminates under in - plane shear [J]. CompositeScience Technology, 1998,58(12) : 1949-1960. |
| [8] | Kumar D,Singh S B. Postbuckling strengths of compositelaminate with various shaped cutouts under in-plane shear [J],Composite Structures, 2010. 92(12) : 2966-2978. |
| [9] | Kumar D, Singh S B. Effects of boundary conditions onbuckling and postbuckling responses of composite laminatewith various shaped cutouts [J]. Composite Structures,2010,92(3): 769-779. |
| [10] | Guo S, Zhou L, Cheung C W. Cutout reinforcements for shearloaded laminate and sandwich composite panels [J], Int JMech Mater Des, 2008, 41: 57-71. |
| [11] | Guo S J. Stress concentration and buckling behaviour of shearloaded composite panels with reinforced cutouts [ J ].Composite Structures, 2007,80(1) : 1-9. |
| [12] | 王丹勇,温卫东,崔海涛.含孔复合材料层合板静拉伸三维逐渐损伤分析[J].力学学报,2005,37(6): 788-795. |
| [13] | 韩小平,郭章新,朱希平,等.含孔复合材料层合板孔边的力集中[J].复合材料学报,2009,26(1): 168-173. |
| [14] | 韩小平,曹效昂,朱西平,等.孔口缝合补强对含孔层板应变集中影响的试验研究[J].复合材料学报,2006,23(4): 169-174. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%