研究了碳的质量分数低于0.3%、不同硅含量的Mn系贝氏体钢的冲击韧性随回火温度的变化,结果表明,随着Si含量的提高,低温回火阶段出现韧性峰值的温度由220℃提高至340℃,韧性出现低谷的温度由340℃提高至520℃,这与Si抑制碳化物析出、稳定残余奥氏体有关.低Si钢一般适合高温回火后使用,高Si钢一般适合低温回火后使用;但碳的质量分数低于0.08%时,无论Si含量如何,低温或高温回火均适用,若碳含量过高,回火改善韧性的作用不明显.
Impact-toughness of Mn-series bainitic steel with carbon content less than 0.3% and different silicon content after tempering were studied.The results show that the temperature of peak value of toughness increases from 220℃ to 340℃ with increasing of the silicon content during stage of low temperature tempering,and the temperature of valley value of toughness increases from 340℃ to 520℃.It is related to the characteristics of Si that it can stable residual austenite,and inhibit precipitating of carbide.The steel may exhibit perfect toughness with low content of Si after tempered at high temperature,while exhibit good toughness with high content of Si after tempered at low temperature.The steel with carbon content lower than 0.08% can exhibit perfect toughness after tempered at low or high temperature,which iS with no terms of Si.However,for the steel with high carbon content,it can not exhibit good toughness after tempered at any temperature.
参考文献
| [1] | 方鸿生,徐平光,白秉哲,刘东雨,蔡漳平,孙卫华,唐立东.一种新的复相组织--仿晶界型铁素体/粒状贝氏体[J].金属热处理,2000(11):1-5. |
| [2] | 黄维刚;方鸿生;郑燕康 .硅和少量钼对Mn-B系贝氏体钢转变动力学的影响[J].金属热处理,1997,22(10):25. |
| [3] | 黄维刚;方鸿生;郑燕康 .硅对Mn-B系空冷贝氏体钢组织与性能的影响[J].金属热处理学报,1997,18(01):8. |
| [4] | 黄维刚;方鸿生;郑燕康 .回火温度对高硅Mn-B系贝氏体钢强韧性的影响[J].金属热处理学报,1999,20(04):30. |
| [5] | 黄维刚;徐蓉;方鸿生 等.中低碳含硅空冷贝氏体钢的冲击韧性[J].钢铁研究学报,1997,9(02):31. |
| [6] | 桂州 .Mn系中、低碳贝氏体结构钢的制备与性能研究[D].北京:清华大学,2005. |
| [7] | 方鸿生;白秉哲;郑秀华 等.粒状贝氏体和粒状组织的形态与相变[J].金属学报,1986,22(04):A283. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%