在实验室试制了400、460 MPa级耐候钢,结果表明,试验钢屈服强度分别达到450、550 MPa,抗拉强度分别达到545、615 MPa;400 MPa级耐候钢的显微组织以铁素体为主,460 MPa级的以粒状贝氏体为主;400 MPa级的析出物主要是CuS2和TiN,主要强化机制是细晶强化、析出强化;460 MPa级的析出物主要是CuS2和(NbTi)CN,其主要强化机制是细晶强化、析出强化及相变强化.采用电子背散射EBSD技术分析了其晶体学取向,其晶粒间取向主要是大角度晶界.
参考文献
| [1] | 周德光,傅杰,柳得橹,康永林,王忠丙,王元立.CSP薄板表面裂纹的形成机理与预防措施[J].北京科技大学学报,2002(04):403-406. |
| [2] | Y.Kimura .Phase Transformation Mechanism of Fe-Cu Alloys[J].ISIJ International,1997(3):290-295. |
| [3] | 赵西成,于大全.20MnVB钢碳氮化物析出相的研究[J].金属热处理,1999(04):16-18. |
| [4] | 俞德刚.钢的强韧化理论与设计[M].上海:上海交通大学出版社,1990:81. |
| [5] | Okaguchi S;Hashimoto T;Ohtani H.Effect of Nb,V and Ti on Transformation Behavior of HSLA Steel in Accelerated Cooling[M].Thermec Iron and Steel Institute of Japan,1988:330-336. |
| [6] | P. J. Hurley;P. D. Hodgson .Formation of ultra-fine ferrite in hot rolled strip: Potential mechanisms for grain refinement[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(2):206-214. |
| [7] | Hutchinson B.;Lindh E.;Tagashira K.;Ryde L. .Texture in hot rolled austenite and resulting transformation products[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1):9-17. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%