在Gleeble-1500热模拟试验机上对6082铝合金进行多组热压缩试验,得到6082铝合金在350～500℃和0.01 ～5 s-1条件下的流变应力数据.根据试验数据建立基于动态材料模型的6082铝合金热加工图,结合压缩变形后的微观组织观察分析,最终获得试验参数范围内6082铝合金热变形的最佳工艺参数.结果表明:保持较高功率耗散效率的加工安全区集中在变形温度430～490℃、应变速率0.1～0.3 s-1的区域,该区域成形时合金主要发生动态再结晶.根据热加工图及微观组织分析,建议在温度440 ～480℃、应变速率0.1～0.2 s-1范围内选择6082铝合金热成形的工艺参数.
参考文献
| [1] | C. N. Panagopoulos;E. P. Georgiou;A. G. Gavras .Corrosion and wear of 6082 aluminum alloy[J].Tribology International,2009(6):886-889. |
| [2] | 韦韡,蒋鹏,曹飞.6082铝合金的高温本构关系[J].塑性工程学报,2013(02):100-106. |
| [3] | 王岗,尹志民,赵凯,段佳琦,刘博,商宝川.6082铝合金的TTT曲线及其研究[J].材料科学与工艺,2011(04):84-88. |
| [4] | El-Danaf EA;AlMajid AA;Soliman MS .Hot deformation of AA6082-T4 aluminum alloy[J].Journal of Materials Science,2008(18):6324-6330. |
| [5] | LI Xue-song,WU Lai-zhi,CHEN Jun,ZHANG Hong-bing.Static Softening Characteristics and Static Recrystallization Kinetics of Aluminum Alloy A6082 After Hot Deformation[J].上海交通大学学报（英文版）,2010(03):307-312. |
| [6] | Parvizian, F.;Güzel, A.;J?ger, A.;Lambers, H.-G.;Svendsen, B.;Tekkaya, A.E.;Maier, H.J. .Modeling of dynamic microstructure evolution of en AW-6082 alloy during hot forward extrusion[J].Computational Materials Science,2011(4):1520-1525. |
| [7] | 傅高升,陈贵清.3003铝合金热变形机制及其加工图[J].材料热处理学报,2013(02):114-119. |
| [8] | Parasad Y V R K;Seshaeharyulu T .Modeling of hot deformation for microstructural control[J].International Materials Reviews,1998,43(06):243-258. |
| [9] | 苏娟华,杨哲,贾淑果,任凤章,魏世忠.利用加工硬化率方法研究Cu-Cr-Sn-Zn-Ce合金的动态再结晶[J].材料热处理学报,2013(11):104-108. |
| [10] | E.I.POLIAK;J.J.JONAS .A ONE-PARAMETER APPROACH TO DETERMINING THE CRITICAL CONDITIONS FOR THE INITIATION OF DYNAMIC RECRYSTALLIZATION[J].Acta materialia,1996(1):127-136. |
| [11] | E. I. POLIAK;J. J. JONAS .Initiation of Dynamic Recrystallization in Constant Strain Rate Hot Deformation[J].ISIJ International,2003(5):684-691. |
| [12] | 黄光胜,汪凌云,陈华,黄光杰,张所全.2618铝合金的热变形和加工图[J].中国有色金属学报,2005(05):763-767. |
| [13] | 权国政,王熠昕,陈涛,周杰.基于热加工图的7075铝合金热塑性变形工艺参数优化识别[J].功能材料,2011(09):1673-1677,1681. |
| [14] | 非线性拟合法研究20％TiC-弥散铜复合材料的动态再结晶[J].材料热处理学报,2014(06):213-217. |
| [15] | 鲁世强,李鑫,王克鲁,董显娟,李臻熙,曹春晓.基于动态材料模型的材料热加工工艺优化方法[J].中国有色金属学报,2007(06):890-896. |
| [16] | Bozzini B.;Cerri E. .Numerical reliability of hot working processing maps[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):344-347. |
| [17] | S.V.S. Narayana Murty;B. Nageswara Rao .On the flow localization concepts in the processing maps of IN718[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1999(1):159-161. |
| [18] | P. Cavaliere .Hot and warm forming of 2618 aluminium alloy[J].Journal of Light Metals,2002(4):247-252. |
| [19] | Gronostajski Z .The deformation processing map for control of microstructure in CuAl19.2Fe3 aluminum bronze[J].Journal of Materials Processing Technology,2002,125/126:119-124. |
| [20] | 金泉林.铝合金6061的热变形力学行为与微观组织演化规律[J].材料热处理学报,2011(06):51-57. |
| [21] | 陈学海,陈康华,董朋轩,彭国胜,梁信.基于加工图的7085铝合金热成形性能研究[J].稀有金属材料与工程,2013(02):273-277. |
| [22] | 张辉,伍豪杰,蒋福林.4045铝合金热变形行为及其加工图[J].湖南大学学报（自然科学版）,2013(08):83-89. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%