Zn-Cr coating was prepared on the surface of sintered NdFeB permanent magnet samples and preparation parameters were established.The anticorrosive property of Zn-Cr coating on NdFeB was studied by whole-immersion test in NaCl solution and compared with that of zinc plating and nickel plating on NdFeB.Open-circuit potential and self-corrosion current of NdFeB samples with and without Zn-Cr coating were measured.The micro-morphology and composition of Zn-Cr coating were analyzed through SEM, XPS, EDS and XRD.The effect of Zn-Cr coating on magnetic property of NdFeB magnet was also investigated.It is exposed that Zn-Cr coating is anodic type coating for NdFeB magnet, and provided substrate electrochemical protection, barrier protection and passivation protection.The anticorrosion property of NdFeB magnet is obviously enhanced by Zn-Cr coating while the magnet property of NdFeB magnet changed little.
参考文献
| [1] | Sugawa M;Fujimura S;Togawa N et al.New material for permanent magnets on a base of Nd and Fe[J].Chinese Journal of Applied Physiology,1984,55(06):2083. |
| [2] | Willman C J;Narasimhan K S V L .Corrosion characteristics of Re-Fe-B permanent magnets[J].Chinese Journal of Applied Physiology,1987,61(08):3766. |
| [3] | Minowa T.;Yoshikawa M. .Improvement of the corrosion resistance on Nd-Fe-B magnet with nickel plating[J].IEEE Transactions on Magnetics,1989(5):3776-3778. |
| [4] | 张万里,彭斌,蒋洪川,张文旭,杨仕清.粘结NdFeB永磁体化学镀Ni-Cu-P防护层工艺过程研究[J].中国稀土学报,2003(03):351-354. |
| [5] | Zhang Shoumin;Zhou Yongqia .Electroplating of aluminum onto NdFeB magnet from AlCl3+LiAlH4 organic solution[J].Acta Scientiarum Naturalium Universitatis Jilinensis,1999,32(02):14. |
| [6] | 张虹,白书欣,李顺,谭春林.烧结NdFeB磁体热浸镀55Al-Zn合金研究[J].金属热处理,2003(11):22-25. |
| [7] | 贺琦军,李卫.钕铁硼永磁材料防腐蚀研究发展[J].金属功能材料,2001(05):8-13. |
| [8] | 于升学,杨雪梅,杨洪生.Nd-Fe-B永磁体化学镀Ni-Cu-P工艺研究[J].稀土,2002(02):71-72. |
| [9] | 王昕,张春丽.烧结型钕铁硼电镀锌工艺研究[J].表面技术,2003(04):40-43. |
| [10] | Krause Heringer H.Dacromet-a new corrosion resistant metal[M].Product Finishing,1977:29. |
| [11] | 于升学,陈玲,李宁.烧结式锌铝涂层的粘结原理研究[J].电镀与环保,2001(05):20-21. |
| [12] | Zhang Weiming .Application prospect and development of Zn-Cr coating[J].Plating and Surface Finishing,1996,18(06):19. |
| [13] | Sun Hemin .Zinc-chromium film-A new technology of surface treatment for steel[J].Materials Protection,1994,27(08):21. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%