用5.0 mass%的NaCl水溶液对泡沫SiC/Cu双连续相复合材料和对应的基体材料纯铜进行盐雾腐蚀实验.采用腐蚀失重法、扫描电子显微镜和X射线衍射仪对比研究这两种材料的腐蚀行为.结果表明：两种材料的腐蚀产物成分相同,为“铜绿”Cu2Cl(OH)3(碱式氯化铜),下层为Cu2O保护层；在NaCl水溶液中,该复合材料比纯铜材料的腐蚀敏感性大,主要是因为在含氧的Cl-水溶液中该复合材料的结构特性致使泡沫筋微孔中和两相界面处的Cu严重腐蚀.
The corrosion behavior of foamed SiC/Cu co-continuous composite and the corresponding matrix material Cu was examined by 5.0% NaCl salt spray and then characterized by means of weight-loss,SEM and XRD. The results show that the outer corrosion products of the two materials are the same,aeruginosa Cu2Cl(OH)3 and the inner layer is Cu2O, a protective layer.The foamed composite is corroded faster than pure copper in NaCl aqueous solution.It could be mainly attributed to the special structure of the foamed SiC/Cu co-continuous composite.Copper in micropores of foam strut and at two-phase interface suffers severe corrosion in oxygenated aqueous solution containing Cl-.
参考文献
| [1] | 谢素箐,曹小明. 三维网络SiC增强铜基复合材料的干摩擦磨损性能[J]. 摩擦学学报, 23(2):86 [2] Ahmad Z. Mechanism of localized corrosion of aluminum-silicon carbide composites in a chloride containing environment[J]. Journal of Materials Science, 35:2573 [3] Arsenault R J,et al. Microstructure of fiber and particulate SiC in 6061Al composites[J]. Scrip Metall, 17:67[4]Sennur Candan,Effect of SiC particle size on corrosion behavior of pressure infiltrated Al matrix composites in a NaCl solution［J］.Materials Letters,2004,58:3601.[5]Saraswathi Y L,Das S,Monda D P.Influence of microstructure and experimental parameters on the erosioncorrosion behavior of Al alloy composites［J］.Materials Science and Engineering A 2006(425):244.[6]Shen B,Hu W,Liu L,Zhou W,et al.Metal-matrix interpenetrating phase composites produced by squeeze casting［J］.Transactions of Nonferrous Metals.Society of China,2002,12(1):26.[7]黄秉升.盐雾试验标准及其实施.涂料工业,2002,32(12):39.[8]徐明德,刘颖.金属腐蚀与防护标准手册［M］.北京：中国环境科学出版社,1996.352.[9]夏兰廷.金属材料的海洋腐蚀与防护［M］.北京：冶金工业出版社,2003.207. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%