通过试验确定了复合轧制温度等工艺参数,计算了Ti-Zr-Mo(TZM)板累积轧制复合过程变形抗力及轧制力,并对累积复合轧制过程各道次TZM复合板进行了性能测试和组织分析.结果表明:经过三次累积复合的材料抗拉强度和界面结合状态最佳,随累积变形量的增加,复合板晶粒显著细化,晶粒断面直径200 ～500 nm,晶粒在轧制过程中被拉长、展宽,轧制横断面上组织分布均匀化.轧制复合工艺可使TZM板材抗拉强度提高50％,2 mmTZM复合板最高抗拉强度可达968 MPa,伸长率2.0％.
参考文献
| [1] | Langdon T G;Furukawa M;Horita Z et al.Using intense plastic straining for high strain rate superlasticity[J].JOM-Journal of the Minerals Metals and Materials Society,1998,50(06):41-53. |
| [2] | Niranjani V L;Hari Kumar K C;Subramanya Sarma V .Development of high strength Al-Mg alloy through cold rolling and ageing[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2009,515(1-2):169-175. |
| [3] | Saito Y.;Tsuji N.;Sakai T.;Utsunomiya H. .Novel ultra-high straining process for bulk materials - Development of the accumulative roll-bonding (ARB) process[J].Acta materialia,1999(2):579-583. |
| [4] | Hyoung Wook Kim;Suk Bong Kang;Nobuhiro Tsuji .Deformation Textures of AA8011 Aluminum Alloy Sheets Severely Deformed by Accumulative Roll Bonding[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2005(11):3151-3163. |
| [5] | 黄光杰,邹彬,黄鑫,陈泽军,刘庆.累积复合轧制法制备层状超细晶材料的研究现状[J].材料导报,2011(09):6-10,27. |
| [6] | 肖松涛,周廉,王国栋,杜林秀,王国栋,巨建辉.钨板轧制的轧制力模型研究[J].稀有金属材料与工程,2007(07):1219-1223. |
| [7] | 陈程,尹海清,曲选辉,朱琳.钼变形抗力的研究[J].稀有金属材料与工程,2007(07):1237-1240. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%