利用动态热机械分析(DMTA)法研究了东邦HTA和国产CCF-1两种T300级炭纤维(CF)增强QY8911-Ⅰ型双马来酰亚胺(BMI)树脂基复合材料的固化动力学,并用FT-IR和XPS对炭纤维表面上胶剂及官能团进行了分析.结果表明,上胶剂对CF/BMI复合材料的固化反应程度没有明显影响,但除胶前后,复合材料的固化初始松弛时间和反应活化能发生了不同变化,HTA CF除胶后固化初始松弛时间延长,反应活化能增大,而CCF-1 CF除胶后固化初始松弛时间缩短,反应活化能减小,这主要是因为炭纤维表面活性官能团含量的不同所致.
参考文献
| [1] | CHEN W M;YU Y H;LI P et al.[J].Composites Science and Technology,2007,67(11-12):2261-2270. |
| [2] | 郭战胜,杜善义,张博明,张宝艳,陈祥宝.碳纤维/双马树脂预浸料体系的固化动力学[J].化学物理学报,2004(02):219-224. |
| [3] | X.Ramis;A.Cadenato;J.M.Morancho;J.M.Salla .Curing of a thermosetting powder coating by means of DMTA,TMA and DSC[J].Polymer: The International Journal for the Science and Technology of Polymers,2003(7):2067-2079. |
| [4] | SPADAROA G;CALDERAROB E;TOMARCHIOB E et al.[J].Radiation Physics and Chemistry,2005,72(04):465-473. |
| [5] | Martin J.S. .Study of the curing process of a vinyl ester resin by means of TSR and DMTA[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(11):4203-4211. |
| [6] | HSICH H S Y .[J].Journal of Applied Polymer Science,1982,27:3265-3277. |
| [7] | FERNANDEZ B;ABELAIZ A;VALEA A et al.[J].Polymer Composites,2004,25(03):319-330. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%