通过断裂试样断口的宏观和显微分析、显微组织表征、拉伸和冲击试验以及解理断裂应力条件,讨论分析了锌锅用低强度级别钢板弯曲成形断裂的微观解理断裂行为.结果表明,钢板发生解理断裂的微观机制与冲击试样断裂相同,即晶粒尺寸控制的穿过晶界的裂纹扩展是解理断裂的临界事件.粗大的铁素体晶粒的面积分数过高显著降低了裂纹扩展阶段所需的局部解理断裂应力σf.断口宏观分析判断在钢板边部应存在导致应力集中的初始裂纹源,这极大降低了启动解理断裂的断裂应力并同时提高裂纹源前端的正应力σyy,扩大了解理断裂活跃区至初始裂纹前端,从而不可避免地发生脆性解理断裂.
参考文献
| [1] | Rasband W S .Image Processing With ImageJ[J].Biophotonics International,2004,11(07):36. |
| [2] | Vander V G F.ASM Handbook[M].USA:ASM International,1987 |
| [3] | Chakrabarti D .Development of Bimodal Grain Structures and Their Effect on Toughness in HSLA Steel[D].Birmingham:University of Birmingham,2007. |
| [4] | Anderson T L.Fracture Mechanics:Fundamentals and Applications[M].Boca Raton:Taylor and Francis,2005 |
| [5] | Ray A;Sivaprasad S;Chakrabarti D.A Critical Grain Size Concept to Predict the Impact Transition Temperature of Ti-Microalloyed Steels[J].International Journal of Fracture,2012(01):215. |
| [6] | 王国珍,王玉良,轩福贞,涂善东,王正东.加载速率、缺口几何和加载方式对16MnR钢解理断裂行为的影响[J].金属学报,2009(07):866-872. |
| [7] | WANG G Z;LIU Y G;CHEN J H .Investigation of Cleavage Fracture Initiation in Notched Specimen of a C-Mn Steel With Carbides and Inclusions[J].Materials Science and Engineering A,2004,369(1/2):181. |
| [8] | Chakrabarti D;Strangwood M;Davis C .Effect of Bimodal Grain Size Distribution on Scatter in Toughness[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2009,40:780. |
| [9] | Hahn G T .The Influence of Microstructure on Brittle Fracture Toughness[J].Metallurgical Transactions A,1984,15:947. |
| [10] | WANG G Z;CHEN J H .Cleavag Fracture Criterion of Low Alloy Steal and Weld Metal in Notched Specimens[J].International Journal of Fracture,1998,89(03):269. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%