在多元醇媒介中采用溶剂热法合成了油酸/三苯基膦包裹的钴纳米粒子.采用X射线衍射4g(XRD)、透射电镜(TEM)、红外光谱仪(IR)和热重分析仪(TG)对所得样品进行了分析.TEM照片显示所制备的钴纳米粒子粒径约为14nm,分散良好,尺寸分布较窄.XRD分析表明,钴纳米以六角密堆积和面心立方的混晶形式存在.研究发现溶液的pH值对产物有重要影响,即只有当溶液的pH值高于12.62时才可以得到纯的纳米钴.热重分析证实包裹在纳米钴表面的油酸和三本基膦分别占整个纳米粒子质量的25.8%和69.2%.
Oleic acid/triphenylphosphine coated Co nanoparticles are synthesized by solvethermal approach in polyol medium. The as-prepared Co nanoparticles are characterized by XRD,TEM,IR and TG. TEM images show that the average size of the well-dispersed Co nanoparticles are ca,14nm with narrow size distribution. XRD pattern indicates that the Co nanoparticles are presented in the mixed crystal structure of hexagonal close-packed (hcp) phase and face-centered cubic (fcc) phase. The pH value of reaction medium plays an important role in the preparation of cohalt nanoparticles,and when the pH value is as high as 12.62,pure Co can be obtained.The weight contents of oleic acid/triphenylphosphine and pure cobalt of the as-prepared cobalt samples determined by thermogravimetric analysis are ca.25. 8% and 69. 2%,respectively.
参考文献
| [1] | Zhang, HZ;Qiu, JS;Liang, CH;Li, ZL;Wang, XN;Wang, YP;Feng, ZC;Li, C .A novel approach to Co/CNTs catalyst via chemical vapor deposition of organometallic compounds[J].Catalysis Letters,2005(3/4):211-214. |
| [2] | Chinnasamy CN.;Jeyadevan B.;Shinoda K.;Tohji K. .Polyol-process-derived CoPt nanoparticles: Structural and magnetic properties[J].Journal of Applied Physics,2003(10 Pt.2):7583-7585. |
| [3] | Pankhurst QA.;Connolly J.;Jones SK.;Dobson J. .Applications of magnetic nanoparticles in biomedicine [Review][J].Journal of Physics, D. Applied Physics: A Europhysics Journal,2003(13):R167-R181. |
| [4] | Puntes V F;Zanchet D;Erdonmaez C K et al.Synthesis of hep-Co nanodisks[J].Journal of the American Chemical Society,2003,124:12874. |
| [5] | Wang F;Gu H;Zhang Z .Preparation of Co nanocrystals in the homogeneous solution with the presence of a static mag-netic field[J].Materials Research Bulletin,2003,38:347. |
| [6] | Ali Javey;Hongjie Dai .Regular Arrays of 2 nm Metal Nanoparticles for Deterministic Synthesis of Nanomaterials[J].Journal of the American Chemical Society,2005(34):11942-11943. |
| [7] | Chioncel MF;Haycock PW .Structural characterization of cobalt thin films grown by metal-organic CVD[J].Chemical vapor deposition: CVD,2005(5):235-243. |
| [8] | Wu N;Fu L;Su M.Interaction of fatty acid monolay-ers with cobalt nanoparticles[J].Nano Letters,2004(04):383. |
| [9] | Si SF;Li CH;Wang X;Yu DP;Peng Q;Li YD .Magnetic monodisperse Fe3O4 nanoparticles[J].Crystal growth & design,2005(2):391-393. |
| [10] | Li H;Liao SJ .Synthesis of flower-like Co microcrystals composed of Co nanoplates in water/ethanol mixed solvent[J].Journal of Physics, D. Applied Physics: A Europhysics Journal,2008(6):65004-1-65004-7-0. |
| [11] | Li, H;Liao, SJ .Preparation of large Co nanosheets with enhanced coercivity by a magnetic-field-assisted solvothermal approach free of surfactants, complexants or templates[J].Journal of Magnetism and Magnetic Materials,2009(17):2566-2570. |
| [12] | Murray C B;Sun S;Doyle H et al.Monodisperse 3d transi-tion-metal(Co,Ni,Fe)nanoparticles and their assembly in-to nanoparticle superlattices[J].MRS Bulletin,2001,26:985. |
| [13] | Chakroune N.;Viau G.;Ricolleau C.;Fievet-Vincent F.;Fievet F. .Cobalt-based anisotropic particles prepared by the polyol process[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2003(2):312-318. |
| [14] | Klug H P;L Alexander E.X-ray diffraction procedures for polycrystalline and amorphous materials[M].New York:John Wiley and Sons,Inc,1962:491. |
| [15] | Su Y K;Shen C M;Yang T Z et al.The dependence of Co nanoparticle sizes on the ratio of surfactants and the influ-ence of different crystal sizes on magnetic properties[J].Applied Physics A:Materials Science and Processing,2005,81:569. |
| [16] | Puntes V F;Krishnan K;Alivisatos A P .Synthesis of col-loidal cobalt nanoparticles with controlled size and shapes[J].Topics Catal,2002,19:145. |
| [17] | Yang HT.;Su YK.;Shen CM.;Yang TZ.;Gao HJ. .Synthesis and magnetic properties of epsilon-cobalt nanoparticles[J].Surface and Interface Analysis: SIA: An International Journal Devoted to the Development and Application of Techniques for the Analysis of Surfaces, Interfaces and Thin Films,2004(2):155-160. |
| [18] | Yang H T;Shen C M;Wang Y G et al.Stable cobalt nan-oparticles passivated with oleic acid and triphenylphosphine[J].NANOTECHNOLOGY,2004,15:70. |
| [19] | Luna C;Morales M P;Sema C J et al.Effects of surfac-tants on the particle morphology and self-organization of Co nanocrystals[J].Materials Science and Engineering C:Biomimetic and Supramolecular Systems,2003,23:1129. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%