铝合金牺牲阳极具有许多优点,近年来得到了广泛的应用.介绍了铝合金牺牲阳极材料中常用合金元素的作用、铝合金牺牲阳极的活化机理、主要的几类铝阳极材料、铝合金牺牲阳极应用概况以及发展前景.
参考文献
| [1] | Reding J T;Newport J J .[J].材料保护,1966,5(12):15. |
| [2] | Gurrappa I .[J].Corrosion Prevention & Control,1997,44(03):69. |
| [3] | Keir D S;Pryor M J;Sperry P R .[J].Journal of the Electrochemical Society,1967,114:777. |
| [4] | Despic A R;Drazic D M;Purenovic M M et al.[J].Journal of Applied Electrochemistry,1976,6(06):527. |
| [5] | Reboul M C;Gimenez P H;Rameau J J .[J].Corrosion,1984,40(07):366. |
| [6] | Tuck C D S;Hunter J A;Scamans G M .[J].Journal of the Electrochemical Society,1987,134:2970. |
| [7] | Breslin C B;Carroll W M .[J].Corrosion Science,1992,33(11):1735. |
| [8] | Carroll W M;Breslin C B .[J].Corrosion Science,1992,33(07):1161. |
| [9] | 孙鹤建;火时中 .[J].中国腐蚀与防护学报,1987,7(02):115. |
| [10] | Gurrappa I .[J].Corrosion Prevention & Control,1993,40(05):111. |
| [11] | Kulkarni A G;Gurrappa I .[J].British Corrosion Journal,1993,28(01):67. |
| [12] | Reding J T .[J].Materials Performance,1971(10):17. |
| [13] | 李启中.金属电化学保护[M].北京:中国电力出版社,1997:45. |
| [14] | 蔡钦友.[J].腐蚀与防护,1985(04):22. |
| [15] | 侯保荣.海洋腐蚀与防护[M].北京:科学出版社,1997:104. |
| [16] | 唐和清 .[J].化工腐蚀与防护,1990,18(01):1. |
| [17] | 朱承德.新型高效牺牲阳极的研制[J].材料保护,1997(08):21. |
| [18] | 齐公台,郭稚弧,魏伯康.不同锡含量高温铝基牺牲阳极的电化学性能[J].材料保护,1999(10):29-30. |
| [19] | Tamada A;Tamura Y .[J].Corrosion Science,1993,34(02):261. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%