以Co(NO3)2·6H2O、Ca(NO3)2·4H2O为原料,NaOH为沉淀剂,采用化学共沉淀方法制备了前驱物.该前驱物预烧后,利用SPS进行烧结获得纯相Ca2Co2O5块体.分别采用DTA-TG、XRD和SEM对前驱体的热分解过程、Ca2Co2O5的形成过程进行了表征,并对其热导率进行了测试.结果表明:在Ph=13.20获得所需化学计量比的前驱物.该前驱物在700～800℃预烧2h后,采用SPS烧结.烧结温度为800℃,压力30MPa,保温时间5min,可以获得纯相Ca2Co2O5块体.断口形貌为层状,晶粒长约1.4μm.热导率随温度的升高而降低.
参考文献
| [1] | Nakarsugawa H;Iguchi E .[J].Materials Letters,2002,53:221-226. |
| [2] | Moon J W;Masuda Y;Seo W S et al.[J].Materials Letters,2001,48:225-229. |
| [3] | Minemi H;Itaka K;Kawaji H et al.[J].Applied Surface Science,2002,8044:1-6. |
| [4] | Li S.;Matsubara I.;Ueno K.;Sodeoka S.;Yamada H.;Funahashi R. .Thermoelectric properties of oxides Ca2Co2O5 with Bi substitution[J].Journal of Materials Science Letters,2000(15):1339-1341. |
| [5] | Li S;Funahashi R;Mastubara I.Thermoelectric Properties of Oxides Ca2Co2O5 with Bi Substitution[A].,1999:581-583. |
| [6] | Siwen L;Ryoji F;Ichilo M et al.[J].Ceramics International,2001,27:321-324. |
| [7] | 张久兴,刘科高,周美玲.放电等离子烧结技术的发展和应用[J].粉末冶金技术,2002(03):129-134. |
| [8] | Zhou Aiguo;Wang Chang-an;Hunag Yong .[J].Journal of Materials Science,2003,38:3111-3115. |
| [9] | 罗锡裕.放电等离子烧结材料的最新进展[J].粉末冶金工业,2001(06):7-16. |
| [10] | Ichiro M;Ryoji F;Tomonari T et al.[J].Journal of Applied Physics,2001,7(90):462-465. |
| [11] | Xu Gaojie;Ryoji F;Masahiro S et al.[J].Solid State Communications,2002,124:73-76. |
| [12] | Shin T;Toshihiko T;Shinya I et al.[J].Materials Science and Engineering,2001,B86:20-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%