在常温常压下以Cu-Zn-Al合金为基体,用混合酸适当处理,制得了两种不同形貌、结构新颖的一维合金纳米结构.通过透射电子显微镜对它们的形貌和结构进行观察,发现其为中空圆柱结构,接近纳米管,但管壁较厚,中空程度小.根据EDX以及选区衍射确定了产物为一维Cu-Zn-Al合金纳米结构.初步分析了一维Cu-Zn-Al合金纳米结构的形成机理.
参考文献
| [1] | Iijima S .[J].Nature,1991,354:56. |
| [2] | Nath M.;Rao CNR.;Govindaraj A. .Simple synthesis of MoS2 and WS2 nanotubes[J].Advanced Materials,2001(4):283-286. |
| [3] | Liao HW.;Zhang SY.;Qian YT.;Wang YF. .A solution low-temperature route to MoS2 fiber[J].Chemistry of Materials,2001(1):6-8. |
| [4] | Chen J;Li S L;Xu Q.[J].Chemical Communications,2002:1722. |
| [5] | Rothschild A;Poppvitz-Biro R;Lourie O et al.[J].Journal of Physical Chemistry B,2000,104:8976. |
| [6] | 李镇江,李贺军,陈小龙,李克智,曹永革,李建业.低维GaN纳米材料的最新研究进展[J].稀有金属材料与工程,2002(05):321-324. |
| [7] | Zhou Guangwen;Zhang Ze;Yu Dapeng .[J].Chinese Science A,1999,29(01):85. |
| [8] | Li Y D;Wang J W;Deng Z X et al.[J].Journal of the American Chemical Society,2001,123(40):9904. |
| [9] | Yu DP.;Ding Y.;Hang QL.;Zhang HZ.;Wang JJ.;Zou YH.;Qian W. Xiong GC.;Zhou HT.;Feng SQ.;Bai ZG. .Nanoscale silicon wires synthesized using simple physical evaporation[J].Applied physics letters,1998(26):3458-3460. |
| [10] | Han W Q;Fan S S;Li Q et al.[J].Science,1997,277:1287. |
| [11] | Kondo Y;Takayanagi K .[J].Science,2000,289:606. |
| [12] | Pan Z W;Dai Z R;Wang Z L .[J].Science,2001,291:1947. |
| [13] | Givargizov E I .[J].Cryst Growth,1973,20:217. |
| [14] | Gorbunav A;Jost O;Pompe W .[J].GraffA Carbon,2002,40:113. |
| [15] | 程开甲,程漱玉.论固体膜形成纳米管的机理[J].稀有金属材料与工程,2003(10):773-776. |
| [16] | Gao H X;Liu W H;Li B Y et al.[J].天津大学学报,1997,30:567. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%