本文采用了快冻法、自然浸泡法以及干湿循环方法来研究了碳化行为对混凝土材料的抗冻性、抗氯离子扩散性以及抗硫酸盐侵蚀性的影响作用.试验结果表明碳化后的混凝土试件抗冻性有所提高,但是抗氯离子扩散性变差.同时发现,碳化混凝土试件在经历硫酸盐干湿循环后抗折强度损失大于未碳化试件,降低混凝土的抗硫酸盐侵蚀性能.
参考文献
| [1] | F. Bouchaala;C. Payan;V. Gamier .Carbonation assessment in concrete by nonlinear ultrasound[J].Cement and Concrete Research,2011(5):557-559. |
| [2] | 元成方,牛荻涛,陈娜,段付珍.碳化对混凝土微观结构的影响[J].硅酸盐通报,2013(04):687-691,707. |
| [3] | P. Castro;E.I. Moreno .Influence of marine micro-climates on carbonation of reinforced concrete buildings[J].Cement and Concrete Research,2000(10):1565-1571. |
| [4] | 元成方,牛获涛,齐广政.干湿循环机制下碳化混凝土氯离子侵蚀试验研究[J].西安建筑科技大学学报（自然科学版）,2012(03):339-344,375. |
| [5] | B.Reddy;G.K.Glass;P.J.Lim .On the corrosion risk presented by chloride bound in concrete[J].Cement & concrete composites,2002(1):1-5. |
| [6] | Ha-Won Song;Seung-Jun Kwon .Permeability characteristics of carbonated concrete considering capillary pore structure[J].Cement and Concrete Research,2007(6):909-915. |
| [7] | 刘志勇,吕永高,周新刚,孙伟.含氯盐混凝土碳化过程钢筋锈蚀阈值与使用寿命预测[J].工业建筑,2005(10):50-53. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%