FGH 95 is a powder metallurgy (P/M) processed superalloy, which was developed in the 1980s in China.One of the applications of FGH 95 was high pressure turbine blade retainers. The manufacturing processes used to produce FGH 95 blade retainers consisted of atomization by plasma rotating electrode process (PREP), hot isostatic pressing (HIP) at super-solvus temperature and a sub-solvus solution heat treatment. The material had an equiaxed grain structure (ASTM 6.5-7.5). The γ' precipitates in as-HIP FGH 95 showed a tri-model distribution. Carbides in the alloy were MC type and precipitated at grain boundaries. The prior particle boundaries (PPB) in the material originated mainly from γ' phase. Statistics of the mechanical properties data from batch production of the FGH 95 blade retainers were investigated. The as-HIP FGH 95 blade retainers showed high strength at room temperature and 650 ℃, excellent creep resistance and outstanding stress rupture strength at 650 ℃.
参考文献
| [1] | YAN Ming-Gao;LIU Bo-cao;LI Jin-gui.China Aeronautical Materials Handbook,Vol.5[M].北京:中国标准出版社,2001 |
| [2] | 王旭青,何峰,罗学军,呼和,邹金文,汪武祥.热等静压温度对FGH95粉末高温合金显微组织的影响[J].钢铁研究学报,2003(z1):505-507. |
| [3] | Thamburaj R;Kroul A K;Wallace W.Prior Particle Boundary Precipitation in P/M Superalloy[A].Princeton:Metal Powder Industries and the American Powder Metallurgy Institute,1984:635. |
| [4] | Yang W H;Mao J;Wang W X et al.Effects of Heat Treatment on Prior Particle Boundary Precipitation in a Powder Metallurgy Nickel Base Superalloy[J].Advanced Performance Materials,1995,2(03):269. |
| [5] | Bain K R;Gambone M L;Hyzak J M.Development of Damage Tolerant Microstructures in UDIMET 720[A].Warrendale:The Metallurgical Society of AIME,1988:13. |
| [6] | Rao GA;Srinivas M;Sarma DS .Effect of thermomechanical working on the microstructure and mechanical properties of hot isostatically pressed superalloy Inconel 718[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(2):201-212. |
| [7] | ZHANG Ying;ZHANG Yi-wen;LIU Ming-dong.Morphology Characteristic of Inter-particle Rupture in P/M Superalloy[A].北京:冶金工业出版社,2007:645. |