以磁铁矿精矿粉为原料,配加合适比例的膨润土和石灰石进行造球,通过正交试验分析预热温度、预热时间、预热风量等因素对预热球团强度的影响.结果表明:对预热强度影响程度大小的顺序为预热温度、预热时间、预热风量;3个因素对预热球团强度影响趋势一致,即随着温度的升高,时间的增加,风量的增大,球团强度增大.从工业应用的综合因素考虑,本次试验最优预热制度选取温度为1 000℃,时间为7.5 min,风量为18m3/h.
Pelletizing experiments were carried out by using magnetite concentrate as raw material and adding appropriate proportion of bentonite and limestone for pelletizing.Through orthogonal test,effects of preheating temperature,preheating time and preheating air volume on the strength of preheated pellet were analyzed.Results show that the influence degree order of each factor on preheated pellet strength is in turn preheating temperature,preheating time,preheating air volume.The effect trend of the three factors on preheated pellet strength is basically consistent and its main features are as follow:with the increase of preheating temperature,preheating time and preheating air volume,preheated pellet strength increases.Considering industrial application,the ideal pellet preheating system is 1 000 ℃ of preheating temperature,7.5 minutes of preheating time and 18 m3/h of preheating air volume.
参考文献
| [1] | 乔庭明,郑志强,江巨贞,谷传海.竖炉球团配加巴西精矿的生产试验[J].烧结球团,2001(01):15-17. |
| [2] | 赵忠文.济钢竖炉球团生产30年回顾[J].钢铁,1999(05):1-4. |
| [3] | 付菊英;姜涛;朱德庆.烧结球团学[M].长沙:中南工业大学出版社,1996:1-6. |
| [4] | 张一敏.球团矿生产技术[M].北京:冶金工业出版社,2005:54-56. |
| [5] | 方开泰;马长兴.正交与均匀试验设计[M].北京:科学出版社,2001:1-8. |
| [6] | 熊守安,朱德庆,范晓慧,郭宇峰,白国华,何明华,舒方华.链篦机-回转窑法氧化球团矿试验研究[J].烧结球团,2002(04):1-6. |
| [7] | 张一敏.球团矿生产技术[M].北京:冶金工业出版社,2005:62-66. |
| [8] | 孔令坛.中国球团矿的发展[A].大连:全国球团技术协调组,2004:11-14. |
| [9] | 张一敏.球团理论与工艺[M].北京:冶金工业出版社,2002:116-118. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%