采用原位共聚法制备聚DL丙交酯/β-磷酸三钙(PDLLA/β-TCP)复合骨修复材料.以辛酸亚锡作引发剂,将一定比例的β-磷酸三钙与DL丙交酯(DLLA)混匀后在真空体系下开环聚合,并持续均匀振荡,得到PDLLA/β-TCP复合材料.通过扫描电镜(SEM)、能谱分析(EDS)表征复合材料的有机-无机界面及整体复合情况;通过复合材料中PDLLA分子量及复合材料力学强度的测试考察了β-TCP的较佳加入量.研究发现:复合材料中β-TCP在PDLLA基质中分布均匀,有机-无机界面结合紧密;β-TCP比例越大,复合材料中PDLLA分子量越小;β-TCP对材料强度有增强作用,当β-TCP比例为30 wt%时,复合材料抗压强度可达99 MPa,抗弯强度可达76 MPa.
参考文献
| [1] | 胡运生,范清宇,周勇.骨组织工程学的研究概况及发展趋势[J].当代医学,2001(08):66-71. |
| [2] | Mooney D J;Mazzoni C L;Breuer C et al.Stabilized polyglycolic acid fiber-based tubes for tissue engineering[J].Biomaterials,1996,17:115. |
| [3] | Shastri VP;Martin I;Langer R .Macroporous polymer foams by hydrocarbon templating.[J].Proceedings of the National Academy of Sciences of the United States of America,2000(5):1970-1975. |
| [4] | Calandrelli L.;Malinconico M.;Volpe MG.;Oliva A.;Della Ragione F.;Immirzi B. .Preparation and characterisation of composites based on biodegradable polymers for "in vivo" application[J].Polymer: The International Journal for the Science and Technology of Polymers,2000(22):8027-8033. |
| [5] | 全大萍,卢泽俭,李世普,袁润章.聚DL-丙交酯/羟基磷灰石（PDLLA/HA）复合材料（I）：制备及力学性能[J].中国生物医学工程学报,2001(06):485-488,515. |
| [6] | Nam YS;Yoon JJ;Park TG .A novel fabrication method of macroporous biodegradable polymer scaffolds using gas foaming salt as a porogen additive.[J].Journal of biomedical materials research, Part B. Applied biomaterials,2000(1):1-7. |
| [7] | 王克敏,李世荣,郭嘉.热致相分离技术制备组织工程支架[J].化学与生物工程,2006(01):1-3. |
| [8] | Kulkarni R K;Moore E G;Hegyeli A F et al.Biodegradable poly (lactic acid) polymers[J].Journal of Biomedical Materials Research,1971,5:169. |
| [9] | 王玥华,张云,尹光福,周大利,蒋毅,李勇.用磷酸八钙前驱体法制备β-磷酸三钙[J].航天医学与医学工程,2004(04):266-269. |
| [10] | Donald Garlottal .A literature review of poly(lactic acid)[J].J Polym Env,2001,9(02):63. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%