为扩大碳化铝在导电材料方面的应用,研究稀土碳化钼Ln_xMo_yC的制备方法及其导电性.采用稀土多元渗法,以(NH_4)_3[CrMO_6O_(24)H_6]·7H_2O为前驱体制备Ln_xMo_yC.用X射线衍射、电子探针X射线能谱、光电子能谱和四探针电极等手段对其结构、元素含量、价态及电性能等进行测试.结果表明:生成的L_xMo_yC是六方密堆结构;渗入的微量稀土元素对其导电性产生了影响;La_(0.00593)Nd_(0.00562)Sm_(0.00502)Gd_(0.00500)Mo_(1.98)C(简写为LNSGMC)的室温电导率(4.692×10~(2S·cm~(-1)比用传统方法得到的最高值(1.025×10~-2S·cm~(-1)高近4.6倍,且在289～490K范围内其表现出金属导电行为,在490～550 K范围内却表现出显著的半导体导电行为.
In order to extend the application of Mo_2C as electric materials, the preparation of RE molybdenum carbide Ln_xMo_yC by means of rare earth co-permeation with (NH_4)_3[CrMo_6O_(24)H_6]·7H_2O as the precursor and its conductivity were studied.XRD,EDS,XPS and four-probe poles were used to characterize the structure, element content, valences and conductivity bf Ln_xMo_yC. Results show that the structure of the prepared L_xMo_yC is single hexagonal close-packed (hcp) and some rare earth elements such as Nd, Gd, La and Sm permeated into crystal phase of molybdenum carbide have influence on its conductivity. The conductivity of LNSGMC La_(0.00593)Nd_(0.00562)Sm_(0.00502)Gd_(0.00500)Mo_(1.98C) at room temperature is 1.692×10~2 S·cm~(-1),which is 4.6 times higher than the highest value (1.025×10~2S·cm~(-1) by conventional methods. In the range of 289-490 K,it shows meallic conductivity while in 490-550 K range it shouw obvious semiconductor conductivity.
参考文献
| [1] | 李昕,吴丽平,郭元茹.稀土气相扩渗法制备钕-氮化钼及其导电性[J].无机化学学报,2006(10):1911-1915. |
| [2] | 王思波;胡长文;许林.多酸化学导论[M].北京:化学工业出版社,1998 |
| [3] | 张业;李永旺;孙予罕 et al.[J].催化学报,2003,21(02):109. |
| [4] | 赵良仲,刘芬,张琳.LnCu2O4（Ln=Gd,Nd）电子结构的XPS研究[J].物理化学学报,2001(04):310-313. |
| [5] | 曹维成;安耿;刘高杰 et al.[J].中国钨业,2006,30(05):45. |
| [6] | 马红江,颉伟,朱全力,蓝其盈,谭都平.以正己烷为碳源制备碳化钼[J].石化技术与应用,2006(06):468-470. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%