采用前期双渣法、高拉补吹法在210 t转炉上开展了高拉碳法冶炼高碳钢的大工业试验,出钢碳质量分数为0.04%～0.07%.对于非脱磷铁水冶炼高碳钢,脱磷是高碳出钢的关键环节.试验结果表明:前期双渣法5 min内可将铁水中磷的质量分数由0.078%～0.094%降至0.027%～0.038%;高拉补吹法在碳的质量分数为0.8%～1.1%时拉碳,钢水中磷的质量分数为0.014%～0.023%;这2种方法出钢钢水磷含量低,出钢后钢水回磷少,可以实现出钢时碳的质量分数为0.4%～0.7%,满足成品磷的质量分数小于0.015%.高碳条件下炉渣的高氧化性利于钢中磷的去除,实现高碳出钢.高拉碳法上业应用后,高碳钢平均出钢碳的质量分数由原来的0.22%提高到0.40%左右,钢中全氧的质量分数平均降低1.6×10-6,氮的质量分数平均降低5.1×106.
参考文献
| [1] | Nashiwa H;Adochi T;Okazaki T et al.Dephosphorization in BOF at Wakayama Works[J].Ironmaking and Steelmaking,1981,8(01):29. |
| [2] | Mitsushima S;Harguehi T;Ito S .Production of High-Carbon Quality Steel for Special Use[J].Ironmaking and Steelmaking,1977,4(01):29. |
| [3] | Chukwulebe B;Kimushkin A;Kuinetsov G .The Utilization of High-Phosphorus Hot Metal in BOF Steelmaking[J].Iron and Steel Technology,2006,3(11):46. |
| [4] | 刘跃,刘浏,佟溥翘,赵继宇,吴建鹏,李小明,王国平.优质高碳钢高拉碳前期脱磷过程控制[J].炼钢,2006(02):27-29. |
| [5] | 高泽平.转炉冶炼高碳钢的工艺研究[J].钢铁研究,2001(02):13-15,18. |
| [6] | 夏顶忠.复吹转炉冶炼中高碳钢[J].鞍钢技术,1996(04):10. |
| [7] | 任建亭;梁淑华 .酒钢30 t顶吹转炉吹炼高碳钢的冶金反应特性及工艺研究[J].钢铁研究,1996,24(01):3. |
| [8] | 陈家祥.炼钢学原理[M].北京:冶金工业出版社,1999 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%