本文以陶瓷废弃物中的陶质制品和瓷质制品作粗骨料,对不同取代率的陶瓷混凝土的配合比及其立方体抗压强度进行了试验研究,结果表明:水灰比相同时,不同掺量的瓷质混凝土和陶质混凝土抗压强度均能满足同一设计等级普通混凝土的强度要求;陶质混凝土坍落度与普通混凝土接近,瓷质混凝土坍落度随着瓷质粗骨料掺量的增加而增大.
参考文献
| [1] | 崔正龙,童华彬,路沙沙,吴翔宇,汪振双.再生骨料对混凝土透气性及碳化性能的影响研究[J].硅酸盐通报,2013(03):518-522. |
| [2] | RM. Senthamarai;P. Devadas Manoharan;D. Gobinath .Concrete made from ceramic industry waste: Durability properties[J].Construction and Building Materials,2011(5):2413-2419. |
| [3] | 郭远臣,王雪.再生骨料混凝土弹性模量实验研究[J].硅酸盐通报,2013(03):467-471. |
| [4] | Rattapon Somna;Chai Jaturapitakkul;Amde M. Amde .Effect of ground fly ash and ground bagasse ash on the durability of recycled aggregate concrete[J].Cement & concrete composites,2012(7):848-854. |
| [5] | Reusing ceramic wastes in concrete[J].Construction and Building Materials,2010(5):832. |
| [6] | 崔正龙,路沙沙,汪振双.不同强度砂浆界面过渡区对再生骨料混凝土性能的影响[J].硅酸盐通报,2011(03):545-549. |
| [7] | RM. Senthamarai;P. Devadas Manoharan .Concrete with ceramic waste aggregate[J].Cement & concrete composites,2005(9/10):910-913. |
| [8] | J. DE BRITO;A. S. PEREIRA;J. R. CORREIA .Mechanical behaviour of non-structural concrete made with recycled ceramic aggregates[J].Cement & concrete composites,2005(4):429-433. |
| [9] | 万超 .再生陶瓷粗骨料混凝土基本力学性能与碳化试验研究[D].华侨大学,2009. |
| [10] | 毋雪梅,李愿,管宗甫.废弃陶瓷再生混凝土及界面研究[J].郑州大学学报（工学版）,2010(02):35-38. |
| [11] | 古松,雷挺,陶俊林.再生混凝土配合比设计及早期强度试验研究[J].工业建筑,2012(04):1-4. |
| [12] | 张亚梅,秦鸿根,孙伟,郝东明,宁钟.再生混凝土配合比设计初探[J].混凝土与水泥制品,2002(01):7-9. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%