为了探讨1,4-丁炔二醇对纳米晶镍镀层硬度和耐蚀性的影响,采用直流电沉积法在黄铜表面制备了纳米晶镍镀层.利用X7000 X射线衍射仪、FEI Quanta600 FE-SEM扫描电镜、DUH-211S动态超显微微米压痕仪、动电位极化曲线及阻抗谱,研究了不同浓度1,4-丁炔二醇对镍镀层结构、硬度及耐蚀性的影响规律.结果表明:随着镀液中1,4-丁炔二醇浓度的增加,镍镀层晶面的择优取向由(200)织构向(111)转变,晶粒尺寸减小;镍镀层硬度增加,在1,4丁炔二醇浓度为0.5 g/L时达到654 HV;在3.5％NaCl(质量分数)溶液中当1,4-丁炔二醇浓度为0.1 g/L时,镍镀层的耐腐蚀性最好.
参考文献
| [1] | Clark D;Wood D;Erb U .Industrial applications of electrodeposited nanocrystals[J].Nanostructured Materials,1997,9(01):755-758. |
| [2] | 荆天辅,乔桂英,熊毅,邵光杰,于升学,张纯江,侯登振.添加剂对喷射电沉积纳米晶镍的影响[J].材料保护,2001(07):16-17. |
| [3] | Nakamura Y;Kaneko N;Watanabe M et al.Effects of saccharin and aliphatic alcohols on the electrocrystallization of nickel[J].Journal of Applied Electrochemistry,1994,24(03):227-232. |
| [4] | 曾华梁;吴仲达;陈钧武.电镀工艺手册[M].北京:机械工业出版社,1997:189-192. |
| [5] | Mockute D;Bemotiene G .The interaction of additives with the cathode in a mixture of saccharin,2-butyne-1,4-diol and phthalimide during nickel electrodeposition in a Wattstype electrolyte[J].Surface and Coatings Technology,2000,135(01):42-47. |
| [6] | 方景礼.电镀添加剂理论与应用[M].北京:国防工业出版社,2006:16-52. |
| [7] | 张俊,裴和中,张国亮.光亮剂对镍钴合金电铸层的影响[J].材料保护,2009(04):33-35. |
| [8] | 王立平,肖少华,高燕,刘惠文,徐洮.脉冲电流密度对电沉积纳米晶镍织构和硬度的影响[J].电镀与精饰,2005(03):40-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%