为了考察氢键作用对合成水滑石微观结构和热性质的影响，以不同添加比例的乙二醇作为共溶剂，采用水热法制备了水滑石，并利用XRD，SEM，FT-IR，TG-DSC等手段表征／分析了不同乙二醇添加量对水滑石晶体微观结构及热性质的影响，研究表明：在水热体系中添加体积分数约15％的乙二醇共溶剂，可得到结晶更规整的水滑石，当乙二醇添加量增加至60％和90％时，结晶水在水滑石中的水合程度提高，对水滑石的晶体结构和热稳定性影响增大；同时，所得水滑石颗粒形貌趋于不规则、且出现团聚和粘结现象，热分析结果显示，随着乙二醇添加量的增加，层间结合水的释放温度提高，而中间层释放CO2的温度则相应降低。
To investigafe the influence of hydrogen-bond on micro-structure and thermal properties of synthesized Layered double hydroxides '( LDHs), ethylene glycol were used as cosolvent with different addition ratios during the hydrothermal synthesis of LDH. The obtained LDHs samples were characterized using SEM, XRD, FT-IR, and TG-DSC. The comprehensive analysis results indicated that the addition of ethylene glycol with content of approximately 15% (volume ratio) benefited in the achievement of LDHs with better crystal structure and thermal property. In the cases that the addition of ethylene glycol cosolvent further increased to 60% and 90%, the hydration levels of crystal water in the obtained LDHs were elevated. Correspondingly, the influences of crystal water on the ordered-structure as well as the thermal stability were enhanced. At the same time, the aggregation and adhesion among the LDHs particles were shown. Thermal analysis results showed that, with the increasing of ethylene glycol cosolvent, the releasing temperature of crystal water was increased, while that of I carbon dioxide was decreased.
参考文献
| [1] | 申延明,吴静,唐杨军,张惠,王蕾,刘长厚,张振祥.CuMgAl类水滑石的制备与表征[J].硅酸盐学报,2009(02):285-290. |
| [2] | Nyambo C;Kandare E;Wang DY;Wilkie CA .Flame-retarded polystyrene: Investigating chemical interactions between ammonium polyphosphate and MgAl layered double hydroxide[J].Polymer Degradation and Stability,2008(9):1656-1663. |
| [3] | Megha Dadwhal;Mayur M. Ostwal;Paul K T. Liu .Adsorption of Arsenic on Conditioned Layered Double Hydroxides: Column Experiments and Modeling[J].Industrial & Engineering Chemistry Research,2009(4):2076-2084. |
| [4] | Min Wei;Min Pu;Jian Guo .Intercalation of L-Dopa into Layered Double Hydroxides:Enhancement of Both Chemical and Stereochemical Stabilities of a Drug through Host-Guest Interactions[J].Chemistry of Materials: A Publication of the American Chemistry Society,2008(16):5169-5180. |
| [5] | 黄宝晟,李峰,张慧,矫庆泽,段雪,郝建薇.纳米双羟基复合金属氧化物的阻燃性能[J].应用化学,2002(01):71-75. |
| [6] | 任庆利 .液相法合成镁铝水滑石阻燃剂研究[D].西安交通大学,2003. |
| [7] | Masato Shiraga;Tomonori Kawabata;Dalin Li;Tetsuya Shishido;Kenji Komaguchi;Tsuneji Sano;Katsuomi Takehira .Memory effect-enhanced catalytic ozonation of aqueous phenol and oxalic acid over supported Cu catalysts derived from hydrotalcite[J].Applied clay science,2006(3/4):247-259. |
| [8] | Adachi-Pagano M.;Forano C.;Besse JP. .Synthesis of Al-rich hydrotalcite-like compounds by using the urea hydrolysis reaction-control of size and morphology[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2003(8):1988-1993. |
| [9] | 刘亚辉,郭玉华,吴静怡,刘灵燕,何静,陈标华,蒲敏.n（Mg）/n（Al）=3的水滑石层板结构及层间距的阴离子调控[J].高等学校化学学报,2008(06):1171-1175. |
| [10] | 杨士国,陈庆德,沈兴海.乙二醇对反向微乳辐照法制备纳米级氧化亚铜形貌的影响[J].光谱学与光谱分析,2007(11):2155-2159. |
| [11] | Ogawa M.;Kaiho H. .Homogeneous precipitation of uniform hydrotalcite particles[J].Langmuir: The ACS Journal of Surfaces and Colloids,2002(11):4240-4242. |
| [12] | 苟国敬,马培华,褚敏雄.氯离子柱撑复合氢氧化物纳米微晶的制备及属性[J].化学学报,2004(21):2150-2160. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%