研究了TB8钛合金冷轧板材在不同热处理温度和不同保温时间下的晶粒长大行为。结果表明： TB8钛合金冷轧板材在820～880℃的温度范围内不存在晶粒急剧粗化的现象，可以在此区间内的温度下对其进行热处理，保温时间根据温度的不同可在30～120 min范围内选择。此外，借助Beck方程和Arrhenius方程分别计算得到该合金的晶粒生长指数（n）为0.25～0.35，β晶粒长大激活能（Q）为273.23 kJ／mol。
The grain growth behavior of TB8 titanium alloy plate was investigated under different heating temperature and holding time.The results show that the cold-rolled plate of TB8 titanium alloy can be heat treated in the range of 820 ℃ to 880 ℃.The grain rapid coarsening phenomenon does not exist in the above temperature range, and the holding time can be chosen in the range of 30 min to 120 min with different temperatures.Grain growth exponent (0.25~0.35) and grain growth activation (273.23 kJ/mol) are also calculated by Beck and Arrhenius equations.
参考文献
| [1] | 朱知寿,王庆如.TB8钛合金板材冷成形工艺及其应用研究[J].金属学报,2002(z1):414-416. |
| [2] | 叶文君,全桂彝.TB8钛合金板材的焊接性[J].金属学报,2002(z1):302-304. |
| [3] | 周晓虎,马文革,俞汉清,朱知寿.TB8超高强度钛合金热工艺参数研究[J].材料工程,2003(08):37-39,48. |
| [4] | 张青,李萍,薛克敏.TB8合金再结晶组织的分形特征[J].材料研究与应用,2011(01):31-34. |
| [5] | 于腾,王磊,赵永庆,王红才,耿可屏,倪浩天.近β型高强钛合金Ti-26的β晶粒长大行为[J].郑州大学学报（工学版）,2009(01):6-9. |
| [6] | 马英杰,刘建荣,雷家峰,刘羽寅,杨锐.钛合金β晶粒生长规律及晶粒尺寸对损伤容限性能的影响[J].稀有金属材料与工程,2009(06):976-981. |
| [7] | 刘景顺,孙剑飞.渗碳工艺下纯Ti板显微组织及晶粒长大动力学[J].铸造技术,2010(03):284-287. |
| [8] | 姜超,刘雅政,张朝磊,肖金福,张玮,易敏.含铌弹簧钢奥氏体晶粒长大与夹杂物的动态观察及分析[J].特殊钢,2011(01):58-60. |
| [9] | 曾卫东;周义刚;俞汉青.应用Zener-Hollomon因子Ti-17的高温压缩行为[J].西北工业大学学报,1996(02):166-168. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%