研究了Ti-24Al-14Nb-3V-0.5Mo合金压缩时的超塑变形行为和变形过程中的组织变化.结果表明:所研究合金在t=980 ℃、=7.2×10-3 s-1的条件下m值为0.34,压缩时的真应变可大于1.6.在合金的超塑变形初期,O相发生动态再结晶和等轴化过程.随着变形过程的进行,新形成的O相晶粒在B2相中滑动和转动,B2相中的位错运动和界面扩散起调节作用.
参考文献
| [1] | Dutta A;Banerjee D .[J].Scripta Metallurgica et Materialia,1990,24(07):1319. |
| [2] | Yang H S;Jin P;Dalder E et al.[J].Scripta Metallurgica et Materialia,1991,25(05):1223. |
| [3] | Yang H S;Zelin M G;Valiev R Z et al.[J].Scripta Metallurgica et Materialia,1992,26(11):1707. |
| [4] | Yang H S;Mukherjee A K .[J].Materials Transactions,1992,33(01):38. |
| [5] | Ridley N;Islam M F;Pilling J.Structural Intermetallics[J].TheMinerals Metals and Materials Society,1993 |
| [6] | Jobart D;Blandin J J;Varloteaux A et al.[J].Materials Science Forum,1994,170-172:465. |
| [7] | Zhang Y;Ma J;Li X et al.[J].Materials Science Forum,1994,170-172:495. |
| [8] | 王斌;贾天聪;王跃群 等.[J].金属学报,1994,30(07):B309. |
| [9] | Rosenberg Y.;Mukerjee AK. .THE SUPERPLASTIC PROPERTIES OF A TI3AL-NB ALLOY[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1995(0):788-792. |
| [10] | Jobart D;Blandin J J .[J].Materials Science and Engineering A,1996,207(02):170. |
| [11] | Jobart D.;Blandin JJ. .EFFECTS OF HEAT TREATMENTS ON THE MICROSTRUCTURE OF A SUPERPLASTIC TI3AL BASED ALLOY[J].Journal of Materials Science,1996(4):881-893. |
| [12] | Imayev R;Gabdullin N;Salishchev G .[J].Intermetallics,1997,5:229. |
| [13] | Shang B S;Mao W F;Li Z Q .[J].Materials Science Forum,1997,243-245:775. |
| [14] | Jobart D;Blandin J J;Varloteaux A et al.[J].Materials Science Forum,1997,243-245:631. |
| [15] | Fu H C;Huang J C;Wang T D et al.[J].Acta Materialia,1998,46(02):465. |
| [16] | 海锦涛;白秉哲.[A].北京:化学工业出版社,1995 |
| [17] | 刘玉文;刘文俊;刘林生 .[J].金属科学与工艺,1986,5(02):31. |
| [18] | 刘玉文;刘林生;周大军 等.[J].材料科学进展,1989,3(06):494. |
| [19] | 杨光;曾宪文;连建设 等.[J].材料科学进展,1991,5(04):331. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%