为了获得性能更优良的聚乳酸材料,以乳酸、ε-己内酯、丁二酸酐为原料,采用梯度升温法合成了聚乳酸嵌段共聚物,用IPDI对其扩链.采用乌氏黏度法、FT-IR、1H-NMR、TGA及XRD等手段对产物进行了表征.FT-IR和1H-NMR测试结果显示,预期的聚乳酸嵌段共聚物成功合成;几种聚合方法中,以先合成端羟基活性低聚物P(LA-CL),再加丁二酸酐与之共聚合成的产物P(LA-CL/SA)分子量最高,扩链后的产物分子量提高不多;P(LA-CL/SA)的热稳定性比PLA的低;XRD结果显示P(LA-CL/SA)为无定形峰,结晶度比PLA低.与PLA相比,改性后的聚乳酸嵌段共聚物分子量提高,更易降解,柔韧性增加.
参考文献
| [1] | 舒静,王鹏,郑彤,田六一,赵宝秀.熔融缩聚合成聚L-乳酸的研究[J].材料科学与工艺,2007(03):374-378. |
| [2] | Hidto Tsuji;Ippei Fukui .Enhanced thermal stability of poly(lactide)s in the melt by enantiomeric polymer blending[J].Polymer: The International Journal for the Science and Technology of Polymers,2003(10):2891-2896. |
| [3] | Pluta M .Morphology and properties of polylactide modified by thermal treatment, filling with layered silicates and plasticization[J].Polymer: The International Journal for the Science and Technology of Polymers,2004(24):8239-8251. |
| [4] | Ragauskas AJ;Williams CK;Davison BH;Britovsek G;Cairney J;Eckert CA;Frederick WJ;Hallett JP;Leak DJ;Liotta CL .The path forward for biofuels and biomaterials[J].Science,2006(5760):484-489. |
| [5] | Qian HT.;Wang SG.;Bei JZ. .Synthesis, characterization and degradation of ABA block copolymer of L-lactide and epsilon-caprolactone[J].Polymer Degradation and Stability,2000(3):423-429. |
| [6] | 唐文珺,蔡伟.PLLA-PCL无规共聚物的冷变形形状记忆效应[J].功能材料,2007(12):2011-2014. |
| [7] | 白雁斌,王寿峰,雷自强.丁二酸酐与SnCl2·2H2O共催化含水乳酸缩聚制备高分子量聚乳酸[J].高分子学报,2007(05):451-455. |
| [8] | 张建安,吴明元,吴庆云,杨建军,程杰.生物降解材料聚乳酸的合成与表征[J].安徽大学学报（自然科学版）,2008(06):78-81. |
| [9] | 樊国栋,杨海燕,王海花,陈佑宁.聚乳酸均聚物的IPDI/PEG二步法扩链改性研究[J].现代化工,2008(11):52-54. |
| [10] | J.Kylma;J.Tuominen;A Helminen;J.Seppala .Chain extending of lactic acid oligomers.Effect of 2,2'-bis(2-oxazoline) on 1,6hexamethylene diisocyanate linking reaction[J].Polymer: The International Journal for the Science and Technology of Polymers,2001(8):3333-3343. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%