采用粉末冶金法制备六方氮化硼(hBN)含量为8%、10%和12%(质量分数)的Ni-20Cr/hBN自润滑复合材料,研究其在600、700和800℃的高温氧化行为,绘制氧化动力学曲线,并利用XRD和SEM分析氧化层的成分和形貌.结果表明:Ni-20Cr/hBN复合材料在600℃氧化300 h后氧化反应不明显;在700和800℃氧化300 h后出现较明显的氧化产物,主要有Cr2O3、NiCr2O4和CrBO3.氧化反应前100 h的氧化行为符合氧化增量动力学曲线,800℃的氧化抛物线速率常数比700℃的高一个数量级;而氧化100 h后,由于B2O3的熔融,试样质量保持不变或甚至呈下降趋势;在700℃下连续氧化膜基本形成,起到较好的保护作用,在800℃时氧化膜出现不同程度的腐蚀.
@@@@The Ni-20Cr/hBN self-lubricating composites were prepared by powder metallurgy with hBN contents of 8%, 10%and 12%(mass fraction). Its oxidation behaviors were studied in air at 600, 700 and 800℃. The oxidation kinetics curves were gained, and the oxide compositions and morphologies were analyzed by XRD and SEM. The results show that the oxidation of Ni-20Cr/hBN composites oxidized at 600℃for 300 h is not obvious. The oxide products consist of Cr2O3, NiCr2O4 and CrBO3 at 700 and 800℃for 300 h. The kinetic curves of the composites obey the parabolic rate law at the beginning oxidation of 100 h, and the oxidation parabolic rate at 800 ℃ is a magnitude higher than that at 700℃. Meanwhile, the masses of Ni-20Cr/hBN composites become stable or even decrease after 100 h due to melt of B2O3. The oxide scales are complete and do well in protection at 700℃, while are corroded to some extend at 800℃.
参考文献
| [1] | Feng Tao;Li He-Jun;Fu Qian-Gang .Microstructure and anti-oxidation properties of multi-composition ceramic coatings for carbon/carbon composites[J].CERAMICS INTERNATIONAL,2011(1):79-84. |
| [2] | Xinfa Qiang;Hejun Li;Yulei Zhang .Microstructure and anti-oxidation property of Si-W-Cr coating for SiC coated carbon-carbon composites[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2011(25):L249-L253. |
| [3] | 赵双群,董建新,张麦仓,谢锡善.新型镍基高温合金在950℃和1000℃的氧化行为[J].稀有金属材料与工程,2005(02):208-211. |
| [4] | Huang, C.;Zhang, Y.;Vilar, R. .Microstructure and anti-oxidation behavior of laser clad Ni-20Cr coating on molybdenum surface[J].Surface & Coatings Technology,2010(3):835-840. |
| [5] | MA Jun;JIANG Su-meng;GONG Jun;SUN Chao .Composite coatings with and without an in situ forming Cr-based interlayer:Preparation and oxidation behavior[J].Corrosion Science,2011,53(09):2894-2901. |
| [6] | Vialas N;Monceau D .Effect of Pt and Al content on the long-term, high temperature oxidation behavior and interdiffusion of a Pt-modified aluminide coating deposited on Ni-base superalloys[J].Surface & Coatings Technology,2006(7):3846-3851. |
| [7] | Yanjun Wang;Zuomin Liu .Tribological properties of high temperature self-lubrication metal ceramics with an interpenetrating network[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2008(11/12):1720-1726. |
| [8] | Rajnesh Tyagi;Dang Sheng Xiong;Jianliang Li;Jihuai Dai .Elevated temperature tribological behavior of Ni based composites containing nano-silver and hBN[J].Wear: an International Journal on the Science and Technology of Friction, Lubrication and Wear,2010(11/12):884-890. |
| [9] | 王爱芳,张定军,吴有智,王文珍,贾均红.MoS2和石墨对Ni-Cr基复合材料摩擦学性能的影响[J].材料研究学报,2010(05):464-470. |
| [10] | XUE Qun-ji;LIU Hui-wen .The effect of solid lubricants on the tribological behavior of zirconia at high temperatures up to 600℃[J].JournalofPhysics D:A pplied Physics,1997,30(14):1965-1971. |
| [11] | 冯艳,王日初,余琨.Ni-Cr/BN自润滑材料摩擦磨损机理分析[J].稀有金属材料与工程,2007(10):1820-1823. |
| [12] | 蒋冰玉,刘世民,王日初,罗丰华.BN含量对BN/Ni（Cr）自润滑材料力学及摩损性能的影响[J].粉末冶金材料科学与工程,2009(01):57-62. |
| [13] | 薛茂权.石墨含量对镍基高温合金在900 ℃氧化行为的影响[J].稀有金属材料与工程,2009(07):1146-1149. |
| [14] | 薛茂权.含二硫化钼镍铬基高温复合材料的高温氧化行为[J].机械工程材料,2008(09):67-69. |
| [15] | 袁观明,李轩科,董志军,崔正威,丛野.氮化硼掺杂石墨材料的抗氧化性能研究[J].材料导报,2011(22):96-99,110. |
| [16] | 李铁藩.金属高温氧化和热腐蚀[M].北京:化学工业出版社,2003:32-33,203. |
| [17] | 郑学家.硼及硼化合物手册[M].北京:化学工业出版社,2010:6-7. |
| [18] | 刘秀晨;安成强;崔作兴;吴伟.金属腐蚀学[M].北京:国防工业出版社,2002:267-268. |
| [19] | 李维银,刘红飞,赵双群.新型镍基高温合金950℃氧化行为的研究[J].材料热处理学报,2008(03):26-29. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%