Structure and magnetic properties of Fe-based powders prepared by mechanical alloying

金属学报(英文版), 2010, 23(5): 351-356.

^1, , ^2, , ^3, , ^4,

1.Key Laboratory of Special Material and Preparing Technology,Xihua University,Chengdu 610039,China;State Key Laboratory of Electronic Thin Films and Integrated Devices,University of Electronic Science and Technology of China,Chengdu 610054,China

2.Key Laboratory of Special Material and Preparing Technology,Xihua University,Chengdu 610039,China

3.Key Laboratory of Special Material and Preparing Technology,Xihua University,Chengdu 610039,China

4.State Key Laboratory of Electronic Thin Films and Integrated Devices,University of Electronic Science and Technology of China,Chengdu 610054,China

基金项目: Scientific Research Fund of Sichuan Provincial Education Department(08ZA026) State Key Laboratory of Electronic Thin Films and Integrated Devices for support of this work(KFJJ200815)

Structure and magnetic properties of Fe-based powders prepared by mechanical alloying

Tingdong ZHOU ^1, , Zhengyun WANG ^2, , Jiangkang TANG ^3, , Haipeng LU ^4,

2.Key Laboratory of Special Material and Preparing Technology,Xihua University,Chengdu 610039,China

3.Key Laboratory of Special Material and Preparing Technology,Xihua University,Chengdu 610039,China

4.State Key Laboratory of Electronic Thin Films and Integrated Devices,University of Electronic Science and Technology of China,Chengdu 610054,China

Keywords： FeSiAlCr alloy

FeSiAlCr alloy powders were prepared by mechanical alloying,the milling time were 20 h,40 h,60 h and 80 h,respectively.Powders morphology was studied by SEM.Microstructure of powders milled for various times were analyzed by XRD.The complex permittivity and complex permeability of four powders were tested in the frequency range from 0.5 to 18 GHz,and their microwave absorption properties were analyzed.It was found that the particle size of powders milled for 80 h was less than 2 μm.Silicon and aluminum atoms were dissolved into the crystal lattice of iron,and chromium atoms can form alloy with iron atoms.The minimum peak value of reflectivity can reach to -11.3 dB at the frequency of 4.3 GHz for 80 h milling powders,and the other one was -6 dB at 16.5 GHz.

参考文献

[1]	K. Nomura;K. Suzuki;T. Sawada;Y. Ujihira;S. Yoshida .CEMS Study on Fe–Si–Al Alloy Flakes–Polymer Composites[J].Hyperfine Interactions: Journal Devoted to Research in the Border Regions of Solid State, Atomic and Nuclear Physics,2003(1/4):345-350.
[2]	P. Marin;M. Lopez;A. Hernando;Y. Iqbal;H. A. Davies;M. R. J. Gibbs .Influence of Cr additions in magnetic properties and crystallization process of amorphous iron based alloys[J].Journal of Applied Physics,2002(1):374-378.
[3]	T.D. Zhou;P.H. Zhou;D.F. Liang .Structure and electromagnetic characteristics of flaky FeSiAl powders made by melt-quenching[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):545-549.
[4]	B. Zuo;N. Saraswati;T. Sritharan;H.H. Hng .Production and annealing of nanocrystalline Fe-Si and Fe-Si-Al alloy powders[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2004(1/2):210-216.
[5]	L.M. Kubalova;I.A. Sviridov;O.Ya. Vasilyeva .Structural transformation in mechanosynthesized bcc Fe-Al-Si(Ge) solid solutions during heating[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2007(0):467-471.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
在百度学术搜索
在万方数据库搜索
在CNKI搜索

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Structure and magnetic properties of Fe-based powders prepared by mechanical alloying

参考文献