在Na2SiO3-KOH溶液体系中,采用恒流模式在LY12铝合金表面进行了占空比不同、厚度均为50 μm的微弧氧化(Microarc oxidation, MAO)陶瓷膜制备.着重对微弧氧化膜表层、次层、内层以及界面的三维组织结构进行分析,并研究了占空比对陶瓷膜显微结构及相组成的影响.结果表明,大尺寸放电微孔仅在陶瓷膜近表面残存,而次层及内层微孔尺寸明显减小,且临近基体金属侧膜层中γ-Al2O3相较多.陶瓷膜截面能谱分析显示,Si元素在陶瓷膜外层及膜层内部微孔处含量相对较多.占空比对膜层结构影响显著,当占空比较小时陶瓷膜外表面为典型的火山喷射状形貌,随占空比增加,表面呈现出较多尺寸较大的饼状平滑区.陶瓷膜内/外表面XRD分析表明,内/外部膜层中α-Al2O3相含量都随占空比的增加而增加.
参考文献
| [1] | Yerokhin A L et al.[J].Surface and Coatings Technology,1998,110(03):140. |
| [2] | Yerokhin A L et al.[J].Surface and Coatings Technology,1999,122(2-3):73. |
| [3] | 薛文斌,邓志威,张通和,陈如意,李永良.铸造镁合金微弧氧化机理[J].稀有金属材料与工程,1999(06):353-356. |
| [4] | Han Y.;Hong SH.;Xu KW. .Porous nanocrystalline titania films by plasma electrolytic oxidation[J].Surface & Coatings Technology,2002(2/3):314-318. |
| [5] | 周慧 et al.[J].Rare Metal Materials and Engineering (稀有金属材料与工程),2005,34(08):1330. |
| [6] | L. O. Snizhko;A. L. Yerokhin;A. Pilkington;N. L. Gurevina;D. O. Misnyankin;A. Leyland;A. Matthews .Anodic processes in plasma electrolytic oxidation of aluminium in alkaline solutions[J].Electrochimica Acta,2004(13):2085-2095. |
| [7] | 王立世,潘春旭,蔡启舟,魏伯康.等离子体电解氧化过程中单个稳态微放电的热效应研究[J].物理学报,2007(09):5341-5346. |
| [8] | Moon S.[J].Corrosion Science,2009(08):1506. |
| [9] | Current J A et al.[J].Acta Materialia,2006,54(07):1985. |
| [10] | Tian J.;Luo ZZ.;Qi SK.;Sun XJ. .Structure and antiwear behavior of micro-arc oxidized coatings on aluminum alloy[J].Surface & Coatings Technology,2002(1):1-7. |
| [11] | 蒋百灵,朱静,白力静.铝合金微弧氧化陶瓷层在润滑条件下的抗磨性能研究[J].摩擦学学报,2004(03):220-224. |
| [12] | Xue WB.;Lai YC.;Chen RY.;Deng ZW. .Analysis of phase distribution for ceramic coatings formed by microarc oxidation on aluminum alloy[J].Journal of the American Ceramic Society,1998(5):1365-1368. |
| [13] | Current J A et al.[J].Acta Materialia,2006,54(07):1985. |
| [14] | Tillous, K;Toll-Duchanoy, T;Bauer-Grosse, E;Hericher, L;Geandier, G .Microstructure and phase composition of microarc oxidation surface layers formed on aluminium and its alloys 2214-T6 and 7050-T74[J].Surface & Coatings Technology,2009(19):2969-2973. |
| [15] | 薛文斌 et al.[J].Mater Sci & Technol (材料科学与工艺),2000,8(03):41. |
| [16] | 辛世刚,宋力昕,赵荣根,胡行方.微弧氧化Al-Si-O陶瓷涂层的结构与结合强度[J].无机材料学报,2006(02):493-498. |
| [17] | Monfort F et al.[J].Journal of the Electrochemical Society,2005,152(06):382. |
| [18] | 薛文斌,邓志威,陈如意,张通和.LY12铝合金微弧氧化陶瓷膜的纳米压入研究[J].稀有金属材料与工程,2001(04):281-285. |
| [19] | Mcpherson R M .[J].Journal of Materials Science Letters,1973,8(06):851. |
| [20] | 李华平,柴广跃,彭文达,阳英,高敏,郭宝平,牛憨笨.微弧熔区的淬冷过程及其对氧化铝膜微观结构的影响[J].无机材料学报,2008(01):114-120. |
| [21] | 王亚明,雷廷权,蒋百灵,郭立新.交流窄脉冲占空比调制对钛合金微弧氧化陶瓷涂层的影响[J].稀有金属材料与工程,2005(02):329-333. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%