经历相同的服役环境和时间，黄铜HSn70-1A呈现不同的腐蚀现象：一种试样宏观上无明显腐蚀，而另一种试样则发生直径约1mm的穿孔腐蚀．分析表明，腐蚀状况有如此差异的主要原因在于两者的显微组织不同．无明显宏观腐蚀的试样晶粒相对粗大但均匀；而发生穿孔的试样，晶粒相对细小，并有大小不一的情况．这源于加工过程中变形不均匀，最终形成相差悬殊的晶粒状态，使得材料中不可避免地存留有残余应力．因此，腐蚀状况表明合金显微组织决定其局部腐蚀的敏感性．
It is observed that HSnT0-1A brass tubes （70： 30） showed different corrosion behavior under the same service condition for the same time period due to its perculiar microstructure： for example, one showed no local corrosion and the other showed perforation of 1 mm in diameter serviced in fresh water for several months. It was found that the former had larger grians but rather uniform in size. The latter showed a microstructure with finer grains but containing certain larger grains. This kind of microstructure possesses very strong sensitivity for intergranual corrosion and stress corrosion when the alloy tube immersed in fresh water.
参考文献
| [1] | 朱志平,杨道武,周琼花等.凝汽器空冷区铜管汽侧腐蚀研究[J].腐蚀科学与防护技术,2005,17(2):101. |
| [2] | 郑铮.火力发电厂凝汽器铜管的腐蚀与防护[J].材料保护,2004,37(6):59. |
| [3] | 朱志平,陈天江,吴志宏.某热电厂凝汽器铜管汽侧腐蚀原因分析[J].材料保护,1998,31(12):31. |
| [4] | 邓宇强,林卫丽,张祥金等.火力发电厂凝汽器铜管冲刷腐蚀原因[J].腐蚀与防护,2010,31(7):560. |
| [5] | 刘增才,林乐耘,刘少峰.实海暴露黄铜脱锌腐蚀行为及抑制脱锌机理研究[J].腐蚀科学与防护技术,1999,11(2):78. |
| [6] | 毛卫民,赵新兵.金属材料的再结晶和晶粒长大[M].北京:冶金工业出版社,1994:12. |
| [7] | 王德胜,侯英玮.ECAP法对H62黄铜的晶粒细化研究[J].锻压技术,2006(2):39. |
| [8] | 朱远志,饧扬等.高速变形条件下的动态再结晶机制的研究进展[J].铝加工,2000,23(3):43. |
| [9] | 赵冬梅,董企铭,刘平等.Cu-Ni-Si合金在时效过程中析出与再结晶行为[J].功能材料,2002,33(6):618. |
| [10] | 张定栓,何家文.关于x射线衍射法测定微观应力的表征值的讨论[J].金属学报,1998,34(12):1273. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%