采用数值模拟和实验相结合的方法研究了钛合金TC4薄板常规及带热沉的钨极氩弧焊焊接过程中温度及应力应变的分布,考察了热沉对温度场和应力应变场的影响规律,探讨了使用该技术实现应力和变形控制的机理.结果表明:带热沉的钨极氩弧焊焊接过程中,紧随热源之后热沉急冷作用使得试件形成马鞍形温度场,而热沉作用部位温度最低.热沉作用部位的急冷收缩对周围金属产生拉伸作用,使得焊缝及近缝区金属升温过程中产生的压缩塑性应变减小,冷却过程中产生的拉伸塑性应变增大,接头中不协调应变减小,残余应力降低.实验测量与有限元模拟结果吻合良好,证实了采用热沉控制应力与变形的有效性和有限元模型的正确性.
参考文献
| [1] | Joseph R D.Metals Handbook[M].Ohio:Metals Park,1990:634-646. |
| [2] | 萧今声,许国栋.提高高温钛合金性能的途径[J].中国有色金属学报,1997(04):97-105. |
| [3] | 关桥.钛合金薄壁构件的焊接应力与变形[J].国际航空,1979(02):37-41. |
| [4] | Guan Qiao .A survey of development in welding stress and distortion controlling in aerospace manufacturing engineering in china[J].Welding in the World: Journal of the International Institute of Welding: Journal of the International Institute of Welding,1999(1):64-74. |
| [5] | P. MICHALERIS;X. SUN .Finite Element Analysis of Thermal Tensioning Techniques Mitigating Weld Buckling Distortion[J].Welding Journal,1997(11):451s-457s. |
| [6] | Michaleris P;Dantzig J;Tortorelli D .Minimization of welding residual stress and distortion in large structures[J].Welding Journal,1999,78(11):361S-366S. |
| [7] | Dong P;Hong J K;Rogers P .Analysis of residual stresses in Al-Li repair welds and mitigation techniques[J].Welding Journal,1998,77(11):439-445. |
| [8] | Guan Q;Guo D L;Leggat R H .Low stress non-distortion(LSND) welding-a new technique for thin materials[J].Welding International,1994,8(07):41-48. |
| [9] | 关桥;张崇显;郭德伦 .动态控制的低应力无变形焊接新技术[J].焊接学报,1994,15(01):8-15. |
| [10] | Yang Y P;Dong P;Zhang J et al.A hot-cracking mitigation technique for welding high-strength aluminium alloy[J].Welding Journal,2000,79(01):9-S-17-S. |
| [11] | 郭绍庆.随焊激冷减小铝合金薄板的焊接变形[J].焊接,1998(09):8. |
| [12] | 《中国航空材料手册》编辑委员会.航空材料手册[M].北京:中国标准出版社,1988 |
| [13] | 陈楚;汪建华;杨洪庆.数值分析在焊接中的应用[M].上海:上海交通大学出版社,1985 |
| [14] | Massoud K.Principles of Convective Heat Transfer[M].New York:Springer,2001 |
| [15] | 关桥;彭文秀;刘继达 等.焊接热源有效利用率的测试计算法[J].焊接学报,1982,3(01):10-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%