研究交变载荷作用下,在AZ31镁合金疲劳裂纹尖端渗注锆酸盐的沉积行为及其对疲劳裂纹扩展速率的影响.用扫描电镜(SEM)、能谱仪(EDS)及X射线衍射仪(XRD)观察分析裂纹尖端的形貌和物相成分,采取贴应变片方法确定渗注锆酸盐前后应力强度因子的变化.结果表明:锆酸盐转化液能在AZ31镁合金疲劳裂纹尖端形成锆酸盐ZrxOyZnxOy覆层;渗注锆酸盐后裂纹尖端应力强度因子降低约40%,能有效增强疲劳裂纹闭合效应,降低或延滞其疲劳裂纹扩展速率.
参考文献
| [1] | 陈虎.镁合金的研究及其在汽车轻量化中的应用[J].企业技术开发（学术版）,2009(11):17-19. |
| [2] | Z.Y. Nan;S. Ishihara;T. Goshima .Scanning probe microscope observations of fatigue process in magnesium alloy AZ31 near the fatigue limit[J].Scripta materialia,2004(4):429-434. |
| [3] | Sung Hyuk Park;Seong-Gu Hong;Wonkyu Bang;Chong Soo Lee .Effect of anisotropy on the low-cycle fatigue behavior of rolled AZ31magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2010(3):417-423. |
| [4] | Sotomi Ishihara;Zhenyu Nan;Takahito Goshima .Effect of microstructure on fatigue behavior of AZ31 magnesium alloy[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2007(0):214-222. |
| [5] | 范华林,陈平.电磁热效应理论在薄板止裂技术上的应用[J].兵工学报,2005(06):791-794. |
| [6] | 肖福仁,白象忠,乔桂英,栾金雨.电磁热效应对35钢裂纹尖端组织及止裂效果的影响[J].材料热处理学报,2001(02):56-59. |
| [7] | 付宇明,郑丽娟,白象忠.T10钢金属模具中裂纹电磁热止裂的实验研究[J].实验力学,2004(04):488-492. |
| [8] | 沙桂英,刘瑞堂,刘殿魁,姜风春.应力波加载条件下 907A钢-20℃时的动态断裂与止裂研究[J].哈尔滨工程大学学报,2001(01):96-101. |
| [9] | S. ISHIHARA;T. GOSHIMA;Y. YOSHIMOTO .The influence of the stress ratio on fatigue crack growth in a cermet[J].Journal of Materials Science,2000(22):5661-5665. |
| [10] | 任爱国,王晓静,丁静.激光熔覆止裂技术研究[J].表面技术,2006(02):69-71,81. |
| [11] | 邹广平,张学义.一种大量程疲劳试验机实现小试样预制裂纹的方法[J].应用科技,2004(01):49-50,53. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%