研究了Pt/CNT(碳纳米管)电极在动电位和恒电位两种情况下的电化学稳定性. 在动电位条件(0.05～1.2 V vs RHE(可逆氢电极)循环伏安940次, 60 h)下, Pt/CNT电极的电化学表面积下降18.8%;在恒电位条件(1.2 V vs RHE, 60 h)下, Pt/CNT电极的电化学表面积仅下降5.2%. 这表明Pt/CNT电极在动电位条件下性能衰减得更迅速. X射线光电子能谱分析表明,恒电位条件下载体碳纳米管被氧化的程度较大. X射线衍射分析计算表明,动电位和恒电位氧化后, Pt颗粒的平均粒径从3.8 nm分别增大到4.9和3.9 nm. Pt颗粒的长大可能是Pt/CNT电极性能衰减的主要原因之一,而载体的氧化不是Pt/CNT电极性能衰减的主要原因.
参考文献
| [1] | 陈军峰,徐才录,陈贵如,魏秉庆,梁吉,吴德海,毛宗强.碳纳米管表面沉积铂及其质子 交换膜燃料电池的性能[J].中国科学A辑,2001(06):529-533. |
| [2] | 杜秉忱,刘长鹏,韩飞,邢巍,陆天虹,桑革.碳纳米管纯化对Pt/CNTs催化甲醇电化学氧化活性的影响[J].高等学校化学学报,2004(10):1924-1927. |
| [3] | Girishkumar G;Vinodgopal K;Kamat P V .[J].Journal of Physical Chemistry B,2004,108(52):19960. |
| [4] | Li W Zh;Liang Ch H;Zhou W J;Qiu J Sh,Zhou Zh H,Sun G Q,Xin Q .[J].Journal of Physical Chemistry B,2003,107(26):6292. |
| [5] | Kangasniemi K H;Condit D A;Jarvi T D .[J].Journal of the Electrochemical Society,2004,151(04):E125. |
| [6] | 赵新生,孙公权,陈维民,唐水花,辛勤,杨少华,衣宝廉.直接甲醇燃料电池Pt-Ru/C催化剂的稳定性[J].催化学报,2005(05):383-388. |
| [7] | 陈羚,程璇,张颖,彭程,姜燕平,范钦柏.质子交换膜燃料电池性能及催化剂表征[J].厦门大学学报(自然科学版),2003(06):756-762. |
| [8] | 李文震,周振华,周卫江,李焕巧,赵新生,汪国雄,孙公权,辛勤.直接甲醇燃料电池阴极Pt/C催化剂的制备与表征--制备及处理方法的影响[J].催化学报,2003(06):465-470. |
| [9] | Reeve R W;Burstein G T;Williams K R .[J].Journal of Power Sources,2004,128(01):1. |
| [10] | Navessin T;Holdcroft S;Wang QP;Song DT;Liu ZS;Eikerling M;Horsfall J;Lovell KV .The role of membrane ion exchange capacity on membrane vertical bar gas diffusion electrode interfaces: a half-fuel cell electrochemical study[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,2004(1):111-122. |
| [11] | Stevens D A;Dahn J R .[J].Journal of the Electrochemical Society,2003,150(06):A770. |
| [12] | Xing Y Ch .[J].Journal of Physical Chemistry B,2004,108(50):19255. |
| [13] | 邵玉艳,尹鸽平,高云智.二甲醚电氧化增强电化学表面积的研究[J].无机化学学报,2005(07):1060-1064. |
| [14] | 王振波,尹鸽平,史鹏飞.制备过程中缓冲溶液对Pt-Ru/C电催化剂性能的影响[J].催化学报,2005(10):923-928. |
| [15] | Wang Zh B;Yin G P;Shi P F .[J].Carbon,2006,44(01):133. |
| [16] | Maiti A;Ricca A .Metal-nanotube interactions - binding energies and wetting properties[J].Chemical Physics Letters,2004(1/3):7-11. |
| [17] | Furuya N;Ichinose M;Shibata M .[J].Journal of Electroanalytical Chemistry,1999,460(1-2):251. |
| [18] | Ferreira P J;la O' G J;Shao-Horn Y;Morgan D,Makharia R,Kocha S,Gasteiger H A .[J].Journal of the Electrochemical Society,2005,152(11):A2256. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%