通过测量CuCl_2-CuCl-NaCl-HC溶液的氧化还原电位(ORP),研究了酸性蚀刻液在蚀刻过程与电化学再生过程中ORP与溶液组成和温度的关系.结果表明,酸性蚀刻液的ORP随Cu~+离子质量浓度的增加而降低,且在Cu~(2+)离子质量浓度较高或总Cu质量浓度变化不大时与Cu~+离子质量浓度的对数成正比.酸性蚀刻液中的溶解氧、Cu~(2+)离子,Cl~-离子和H~+离子的浓度以及温度对ORP的测量有一定影响,但最大误差不超过0.9%.溶液组成一定时,ORP与测量温度成正比.ORP的测量可以指示酸性蚀刻液的蚀刻速率及其电化学再生过程.
The oxidation reduction potential (ORP) of an acidic etching bath comprising CuCl_2, CuCl, NaCl and HCl was measured, and its dependence on bath composition and temperature during etching and electrochemical regeneration processes was studied. The results showed that the ORP of acidic etching bath is decreased with increasing mass concentration of Cu~+, and is directly proportional to the logarithm of the mass concentration of Cu~+ when the mass concentration of Cu~(2+) is relatively high or when the mass concentration of total Cu varies slightly. The dissolved oxygen in acidic etching bath, as well as the concentration of Cu~(2+), Cl~- and H~+, and temperature have certain impact on ORP measurement, but the maximum error is not more than 0.9%. The ORP is in direct proportion to temperature when the bath composition is unvaried. The measurement of ORP can indicate the etching velocity and electrochemical regeneration process in acidic etching bath.
参考文献
[1] | 江丽.CuCl2蚀刻液制备CuCl的研究[J].环境污染与防治,2000(04):10. |
[2] | 汪晓军,何花,万小芳,崔晓飞.从废蚀刻液中回收资源的应用研究[J].环境工程,2004(02):75-77. |
[3] | 龙义芳.蚀刻废液中铜回收条件的选择及废液再利用[J].环境科学与技术,2006(10):90-91,94. |
[4] | 宋玉亮,廖辉伟.酸性蚀刻废液制备纳米铜粉及其稳定性研究[J].功能材料,2007(06):986-988. |
[5] | 李建华,吴东辉.由CuCl2蚀刻液制取CuCl[J].南通工学院学报(自然科学版),2002(03):17-18,30. |
[6] | 辰光.酸性氯化铜蚀刻液与碱性氯化铜蚀刻液比较[J].印制电路信息,2003(09):38,57. |
[7] | P. Adaikkalam;G.N. Srinivasan;K.V. Venkateswaran .The Electrochemical Recycling of Printed-Wiring-Board Etchants[J].JOM,2002(6):48-50. |
[8] | 曾振欧;黄慧民.现化电化学[M].昆明:云南出版社,1999 |
[9] | 魏静,罗韦因,徐金来,罗海兵.印刷线路板精细蚀刻的影响因素[J].表面技术,2005(02):49-50,55. |
[10] | O. Cakir .Copper etching with cupric chloride and regeneration of waste etchant[J].Journal of Materials Processing Technology,2006(1/3):63-68. |
[11] | 李保松,林安,甘复兴.Ti/IrO2-Ta2O5阳极的制备及其析氧电催化性能研究[J].稀有金属材料与工程,2007(02):245-249. |
[12] | 张招贤.钛电极工学[M].北京:冶金工业出版社,2003 |
[13] | 张志祥.氯酸钠/盐酸型蚀刻铜再生剂之论述[J].印制电路信息,2002(03):40-42. |
- 下载量()
- 访问量()
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%