通过OM,SEM,TEM,XRD和力学拉伸实验,研究了固溶和时效热处理对Mg-12Gd-3Y-Sm-0.5Zr(质量分数,％)合金组织和力学性能的影响.结果表明,Mg-12Gd-3Y-Sm-0.5Zr合金铸态组织由α-Mg基体和含Mg5Gd相和Mg41Sm5相的粗大枝晶组成,经过固溶和时效处理后,时效析出了Mg24Y5相,Mg5Gd相演变为Mg3 Gd相,固溶时效态合金纳米尺寸的长条状相的脱溶析出可有效强化合金.合金在不同状态下的室温抗拉强度为:铸态219.4 MPa、固溶态224.0 MPa和时效态299.8 MPa.
参考文献
| [1] | 周海涛,曾小勤,丁文江,马春江,朱燕萍.Effect of La and Nd on microstructures and mechanical properties of AZ61 wrought magnesium alloy[J].中国有色金属学会会刊(英文版),2004(01):67-70. |
| [2] | Lee Chong Do .Effect of grain size on the tensile properties of magnesium allov[J].Materials Science and Engineering A,2007,459(1-2):355-360. |
| [3] | 郑开云 .Mg-Gd-Nd-Zr系高强耐热镁合金组织与性能研究[D].上海交通大学,2008. |
| [4] | Rokhlin L L;Nikitina N I .Magnesium-gadolinium and magnesium-gadolinium-yttrium alloys[J].ZEITSCHRIFT FUR METALLKUNDE,1994,85(12):819-823. |
| [5] | Ifeanyi Anthony Anyanwu;Shigeharu Kamado;Yo Kojima .Aging Characteristics and High Temperature Tensile Properties of Mg-Gd-Y-Zr Alloys[J].Materials transactions,2001(7):1206-1211. |
| [6] | Ifeanyi Anthony Anyanwu;Shigeharu Kamado;Yo Kojima .Creep Properties of Mg-Gd-Y-Zr Alloys[J].Materials transactions,2001(7):1212-1218. |
| [7] | Qiuming Peng;Xiuli Hou;Lidong Wang;Yaoming Wu;Zhanyi Cao;Limin Wang .Microstructure And Mechanical Properties Of High Performance Mg-gd Based Alloys[J].Materials & design,2009(2):292-296. |
| [8] | 朱蓓蓓,孙扬善,贾迪,薛烽.Mg-Sm系合金的显微组织及力学性能[J].东南大学学报（自然科学版）,2009(03):610-614. |
| [9] | 张清,李全安,井晓天,张兴渊.稀土Sm在耐热镁合金中的应用[J].铸造,2010(03):260-262. |
| [10] | 李全安,李克杰,张清.Sm对时效态Mg-12Gd-2Y-0.5Zr合金组织与力学性能的影响[J].材料热处理学报,2011(12):84-88. |
| [11] | 张清,李全安,井晓天,张兴渊.Mg-10Y-1.5Sm合金的组织和力学性能[J].材料热处理学报,2011(01):24-27. |
| [12] | 李克杰,李全安.Sm和Sb对时效态Mg-12Gd-2Y-0.5Zr合金组织与力学性能的影响[J].材料热处理学报,2011(05):110-115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%