用傅里叶红外光谱法和热分析法研究了双酚A甲醛酚醛环氧树脂(bis-ANER)与甲基六氢邻苯二甲酸酐的固化反应和热性能,结果表明,等温固化反应中环氧基团红外光谱吸收强度随固化时间延长而逐渐减弱;bis-ANER用二氧化乙烯基环己烯锋释后提高了固化产物的玻璃化温度,但降低了热降解温度;固化产物的热降解首先是-OH、-CH2-、-CH3、OC-O和C-O-C的断裂;动态空气气氛下的热降解过程分为两个阶段,起始阶段的热降解反应机理符合一级反应模式.
参考文献
| [1] | Goto K;Hayashi S;Saito T et al.[P].US 20030135011,2003. |
| [2] | Taguchi M;Suzumura Y;Saitou T et al.[P].US 20040034127,2004. |
| [3] | 孙曼灵.环氧树脂应用原理与技术[M].北京:机械工业出版社,2002 |
| [4] | Liu YF;Zhang C;Du ZJ;Li HQ .Preparation and curing kinetics of bisphenol A type novolac epoxy resins[J].Journal of Applied Polymer Science,2006(3):858-868. |
| [5] | Jay R R .[J].Analytical Chemistry,1964,36:667-668. |
| [6] | Rocks J;George G A;Vohwinkel F .[J].Polymer International,2003,52:1758-1766. |
| [7] | Corcuera MA.;Riccardi CC.;Williams RJJ.;Mondragon I. .POLYMER NETWORKS DERIVED FROM THE ANHYDRIDE CURING OF TETRAEPOXIDES[J].Journal of Applied Polymer Science,1997(1):157-166. |
| [8] | Stevens G C .[J].Journal of Applied Polymer Science,1981,26:4259-4278. |
| [9] | Coats A W;Redfern J P .[J].Nature,1964,201:68-69. |
| [10] | Nunez L;Fraga F;Nunez M R et al.[J].Polymer,2000,41:4635-4641. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%