A new technique for preparing TiO2 modified film on carbon steel was accomplished by electroless plating and sol-gel composite process. The artificial neural network was applied to optimize the preparing condition of TiO2 modified film. The optimized condition for forming TiO2 modified film on carbon steel was that NiP plating for 50 min,dip-coating times as 4, heat treatment time for 2 h, and the molar ratio of complexing agent and Ti(OC4HZ9)4 kept 1.5:1. The results showed that TiO2 modified film have good corrosion resistance. The result conformed that it is feasible to design the preparing conditions of TiO2 modified film by artificial neural network.
参考文献
| [1] | PPTrzaskoma-Paulette;ANazeri .[J].Journal of the Electrochemical Society,1997,144(04):1307. |
| [2] | Davepon;JWSchultze;UKonig;CRosenkranz .[J].Surface and Coatings Technology,2003,169-170:85. |
| [3] | CTWu;FHLu .[J].Surface and Coatings Technology,2002,166:31. |
| [4] | X. Nie;A. Leyland;A. Matthews .Deposition of layered bioceramic hydroxyapatite/TiO{sub}2 coatings on titanium alloys using a hybrid technique of micro-arc oxidation and electrophoresis[J].Surface & Coatings Technology,2000(1/3):407-414. |
| [5] | JDKim;SIPyun;MSeo .[J].Electrochimica Acta,2003,48:1123. |
| [6] | EChang;TMLee .[J].Biomaterials,2002,23:2917. |
| [7] | Alexia W. E. Hodgson;Yves Mueller;Dominic Forster;Sannakaisa Virtanen .Electrochemical characterization of passive films on Ti alloys under simulated biological conditions[J].Electrochimica Acta,2002(12):1913-1923. |
| [8] | FStippich;EVera;GKWolf;GBerg Chr Friedrich .[J].Surface and Coatings Technology,1998,103-104:29. |
| [9] | DLee;HHabazaki;AKawashima;KHashimoto .[J].Corrosion Science,2000,42:721. |
| [10] | GuangmingLIU;Meishuan LI;Yanchun ZHOU .[J].Corrosion Science,2003,45:1217. |
| [11] | SKoralov;MYoshimura .[J].Corrosion Science,2003,45:531. |
| [12] | JPearinger;CAOrmec;JLGilbert .[J].BIOMATERIALS,2003,24:1837. |
| [13] | TakaoHanawa .[J].Materials Science and Engineering,1999,267:260. |
| [14] | DJlackwood .[J].Electrochimica Acta,2000,46:563. |
| [15] | HHaazaki;KShimizu;SNagata;P Skeldon, GEThompson , GCWood .[J].Corrosion Science,2002,44:1047. |
| [16] | MKoike;HFujii .[J].Biomaterials,2001,22:2931. |
| [17] | TOhtsuka;TOtsuki .[J].Corrosion Science,2003,45:1793. |
| [18] | JingxiaoLIU;Dazhi YANG;Fei SHI;Yingji CAI .[J].Thin Solid Films,2003,429:225. |
| [19] | CSanchez;Martin In .[J].Journal of Non-Crystalline Solids,1992,147-148:1. |
| [20] | LaizhouSONG;Zhiming GAO;Shizhe SONG .[J].Journal Chinese Society for Corrosion and Protection,2001,21(02):101. |
| [21] | ZhaoyinHOU;Qinglian DAI;Xiaoqun WU .[J].Chinese Journal of Catalysis(in Chinese),1997,18(02):152. |
| [22] | LaizhouSONG;Lijian;Fujun WANG .[J].Materials Science and Technology,2002,10(02):148. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%