为了连接变形镁合金AZ31B,以A1基钎料对变形镁合金AZ31B进行高频感应钎焊.采用扫描电镜、X射线衍射仪、X射线能谱等分析钎焊接头的显微组织及钎缝物相,测试钎焊接头的力学性能及显微硬度.结果表明:在钎焊过程中熔融的Al基钎料与固态的AZ31B母材发生强烈的合金化作用,原始钎料中均一的Mg32(Al,Zn)49相在钎焊后完全消失,同时在钎缝中生成a-Mg、β-Mg17(Al,Zn)12相.钎焊搭接接头的平均抗剪强度达到44 MPa,对接接头的平均抗拉强度达到71 MPa.接头的断裂形式为沿晶脆性断裂,断裂产生在β-Mg17(Al,Zn)12硬脆相处.
参考文献
| [1] | 梁书锦,王欣,刘祖岩,王尔德.AZ31镁合金不同温度挤压后组织性能研究[J].稀有金属材料与工程,2009(07):1276-1279. |
| [2] | 陈振华;严红革;陈吉华.镁合金[M].北京:化学工业出版社,2004 |
| [3] | ALEXANDER E. SHAPIRO .Brazing Magnesium Alloys and Magnesium Matrix Composties[J].Welding Journal,2005(10):33-43. |
| [4] | 张启运;庄鸿寿.钎焊手册[M].北京:机械工业出版社,1999 |
| [5] | 美国钎焊学会.钎焊手册[M].Beijing:National Defenee Industry Press,1982 |
| [6] | Nicholas M G.Joining Processes[M].London,UK:Kluwer Academic Publishers,1998 |
| [7] | Watanabe T;Komatsu S;Oohara K .[J].Welding Journal,2005,84(03):37. |
| [8] | Jacobson D M;Humpston G.Principles of Brazing[M].Ohio:ASM International,Materials Park,2005 |
| [9] | Improving the Soldering of Magnesium Alloys[J].Welding Journal,2006(9):48-51. |
| [10] | Muecklich S;Fritsche G;Wielage B .[J].Welding Journal,2008,87(03):31. |
| [11] | 朱满,杨根仓,刘峰,程素玲,杨伟,万迪庆,周尧和.Al-Mg-Zn二十面体准晶合金中的Frank-Kasper相[J].中国有色金属学报,2006(05):758-761. |
| [12] | Baker H.Alloy Phase Diagrams[M].Ohio:ASM International,Materials Park,2006 |
| [13] | Quan, YJ;Chen, ZH;Gong, XS;Yu, ZH .CO2 laser beam welding of dissimilar magnesium-based alloys[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):45-51. |
| [14] | 金头男,聂祚仁,李斗星.浸渍挤压（SiCw+B4Cp）/Mg（AZ91）复合材料的微观组织[J].中国有色金属学报,2002(01):110-114. |
| [15] | 屠怡范,陈晶益,张波萍,李鹏喜,铃木洋夫.AZ31铸造镁合金的物相和显微组织[J].铸造,2006(05):509-512. |
| [16] | Chi C T;Chao C G;Liu T F et al.[J].Scripta Materialia,2007,56(09):733. |
| [17] | Zhang Z D;Liu L M;Shen Y et al.[J].Materials Characterization,2008,59(01):40. |
| [18] | Coelho RS;Kostka A;Pinto H;Riekehr S;Kocak M;Pyzalla AR .Microstructure and mechanical properties of magnesium alloy AZ31B laser beam welds[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):20-30. |
| [19] | 崔忠圻.金属学与热处理[M].哈尔滨:哈尔滨工业大学出版社,1995 |
| [20] | 郭强,严红革,陈振华,吴有伍.均匀化退火工艺对铸态AZ80镁合金组织与性能的影响[J].金属热处理,2006(07):77-80. |
| [21] | 张菊梅,蒋百灵,王志虎,袁森,夏鹏举.固溶和时效对AZ80镁合金断裂行为的影响[J].特种铸造及有色合金,2007(09):663-666. |
| [22] | 钟群鹏;赵子华.断口学[M].北京:高等教育出版社,2005 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%