研究了在长期约束条件下TiNi合金超弹性的衰减规律,结果表明,超弹性衰减随时间呈类抛物线规律;约束应变越大,衰减量越大,约束应变较小时不发生明显衰减;应力-应变循环处理可显著降低超弹性衰减幅度.在阐明超弹性衰减襄律的基础上,讨论了衰减机制.