研究了镍基高温合金GH4700变形温度和应变速率对热变形行为的影响,建立了该合金的热变形本构方程和热加工图.结果表明:在变形温度1120～ 1210℃、应变速率0.01～20 s-1条件下,该合金的热变形流变曲线呈现出典型的动态再结晶型特征,存在稳态的流变应力,且随着变形温度的升高和应变速率降低,动态再结晶过程更充分;GH4700合金的热变形激活能为326.3165 kJ/mol;该合金在温度为1180～1210℃,应变速率为10 ～ 20 s-1的热压缩变形条件下,能量耗散率η值较高,大于0.30,显微组织发生完全动态再结晶,获得的组织晶粒细小且分布均匀.
参考文献
| [1] | 赵双群,董建新,张麦仓,谢锡善.新型镍基高温合金在950℃和1000℃的氧化行为[J].稀有金属材料与工程,2005(02):208-211. |
| [2] | S.J. Patel.INTRODUCTION TO INCONEL ALLOY 740: AN ALLOY DESIGNED FOR SUPERHEATER TUBING IN COAL-FIRED ULTRA SUPERCRITICAL BOILERS[J].金属学报（英文版）,2005(04):479-488. |
| [3] | Zener C;Hollomon J H .Effect of strain rate upon plastic flow of steel[J].Journal of Applied Physics,1994,15(01):22-26. |
| [4] | P. S. Robi;U. S. Dixit .Application of neural networks in generating processing map for hot working[J].Journal of Materials Processing Technology,2003(1):289-294. |
| [5] | Nho-Kwang Park;Jong-Taek Yeom;Young-Sang Na .Characterization of deformation stability in hot forging of conventional Ti-6Al-4V using processing maps[J].Journal of Materials Processing Technology,2002(0):540-545. |
| [6] | Prasad YVRK.;Seshacharyulu T. .Processing maps for hot working of titanium alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,1998(1/2):82-88. |
| [7] | Srinivasan N;Prasad YVRK;Rao PR .Hot deformation behaviour of Mg-3Al alloy - A study using processing map[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):146-156. |
| [8] | Basinski Z S .Thermally activated glide in face centered cubic metals and its application to the theory of strain hardening[J].Philosophical Magazine,1959,40(04):393-432. |
| [9] | 曾卫东,周义刚,周军,俞汉清,张学敏,徐斌.加工图理论研究进展[J].稀有金属材料与工程,2006(05):673-677. |
| [10] | 杨亮 .690合金变形行为及组织与工艺控制研究[D].北京:北京科技大学,2012. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%