采用2.0mol/L H2SO4溶液为酸性侵蚀介质,在80℃下分别处理1、3、5和10h后得到酸处理的玄武岩纤维样品.利用SEM、EDS、XRD、FT-IR以及拉伸实验等研究酸处理对玄武岩纤维的形貌、成分、物相、分子结构以及力学性能的影响.结果表明,酸处理纤维能基本保持圆柱状形貌,成分趋于只含Si、O；酸处理纤维仍保持玻璃态结构,其指纹区红外吸收峰的峰形更尖锐、峰位移向高频区并出现Si—OH等特点；随着酸处理时间的延长,纤维的断裂强度(模量)保留率均呈下降的趋势,且下降的趋势减缓并趋于稳定.
参考文献
| [1] | Jongsung Sim;Cheolwoo Park;Do Young Moon .Characteristics of basalt fiber as a strengthening material for concrete structures[J].Composites, Part B. Engineering,2005(6/7):504-512. |
| [2] | Lund M .Tensile strength of glass fibres[D].Aalborg:Aalborg University,2010. |
| [3] | Yuanzheng Yue;Martin Korsgaard;Lise Frank Kirkegaard .Formation of a Nanocrystalline Layer on the Surface of Stone Wool Fibers[J].Journal of the American Ceramic Society,2009(1):62-67. |
| [4] | 王广健,郭亚杰,徐明霞.玄武岩纤维生态环境复合滤材过滤性能的研究[J].功能材料,2009(01):130-134. |
| [5] | Guan Su J;Liu H S;Wang L N et al.Study on tensile and melting properties of basalt fiber rcinforced wood plastic composite[J].Journal of Functional Materials,2011,S2:245-247. |
| [6] | 叶邦土,蒋金洋,孙伟,王彩辉.玄武岩纤维对矿物掺合料砂浆性能的影响[J].东南大学学报（自然科学版）,2010(z2):34-39. |
| [7] | Colombo C;Vergani L;Burman M .Static and fatiguc characterization of new basalt fibre reinforced composites[J].Computers & Structures,2012,94(03):1165-1174. |
| [8] | 李建军,党新安.玄武岩连续纤维成形工艺研究[J].材料科学与工艺,2009(02):211-214. |
| [9] | Deak, T;Czigany, T .Chemical Composition and Mechanical Properties of Basalt and Glass Fibers: A Comparison[J].Textile research journal,2009(7):645-651. |
| [10] | 王明超,张佐光,孙志杰,李敏.连续玄武岩纤维及其复合材料耐腐蚀特性[J].北京航空航天大学学报,2006(10):1255-1258. |
| [11] | Wen L;Liang W X;Zhang Z G.The infrared spectroscopy of minerals[M].重庆:重庆大学出版社,1988:71-111. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%