研究了由Ｎｄ_２（Ｆｅ，Ｃｏ）_（１４）Ｂ和Ｎｄ_２（Ｆｅ，Ｃｏ）_（１７）双相组成的ＨＤＤＲ高矫顽力磁粉的微观结构及磁性。发现在单相Ｎｄ_２（Ｆｅ，Ｃｏ）_（１４）Ｂ化合物的基础上降低Ｂ含量，导致Ｎｄ_２（Ｆｅ，Ｃｏ）_（１７）相出现，且随Ｂ含量降低该相逐渐增多．适量的Ｎｄ_２（Ｆｅ，Ｃｏ）_（１７）相的存在对用性有一定有益的作用，过量则导致磁性严重恶化，这可能与该相的尺寸和存在形式密切相关．
The microstructure and magnetic properties of coercive powder prepared by hydrogenation disproportionation desorption recombination method (HDDR) and composed of dual phase Nd2(Fe, Co)14B and Nd2(Fe, Co)17 alloy have been investigated. The decrease in B content in monophase Nd2(Fe, Co)14B alloy induced the formation of Nd2(Fe,Co)17 phase. The remanence Br, of dual alloy Nd12.5 Fe81.5-xCo6Bx with x= 5.2 is higher than that of monophase Nd12.5Fe81.5-xCo6Bx with x=5.88. This may be due to an exchange-coupling interaction between Nd2(Fe, Co)14B and Nd2(Fe, Co)17 phase. Correspondent:( XIAO Yaofu, associate professor, Department of Materials Science, University of Science and Technology Beijing, Beijing 100083)
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | TakeshitaT,NakayamaR．Proc10thIntWorkshoponRareEarthMagnetsandTheirApplications,16-19May,1989,Tokyo,TheSocietyofNon-Traditional,1989:5512McGuinessPJ,ZhangXJ,YinXJ,HarrisIR．JLess-CommonMet,1990 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%