采用机械合金化及氢气氛烧结工艺制备了致密Mo-18%Cu合金;采用粒度分析仪、XRD和SEM等研究了球磨时间对复合粉体粒径、形貌以及烧结温度对烧结体力学性能和断口形貌的影响.结果表明:随着球磨时间的延长,粉体颗粒尺寸不断减小,形貌与相组成合理,球磨60 h效果最好;球磨60 h的混合粉体烧结时,随着烧结温度升高,烧结体密度与力学性能先升后降,在1 350℃烧结2 h性能最好,相对密度达到98.6%,抗弯强度达到581 MPa,硬度达到64 HRC.
参考文献
| [1] | 吕大铭.钼铜材料的开发和应用[J].粉末冶金工业,2000(06):30-33. |
| [2] | John L. Johnson;Randall M. German .Powder metallurgy processing of Mo-Cu for thermal management applications[J].International Journal of Powder Metallurgy,1999(8):39-48. |
| [3] | 南海,曲选辉,方玉诚,何新波.电子封装用注射成形Mo/Cu合金烧结工艺的研究[J].粉末冶金工业,2004(06):1-5. |
| [4] | K. S. Hwang;C. P. Yu;C. K. Yang .Effects of contamination on properties of W-15Cu prepared from mechanically alloyed powders[J].Powder Metallurgy,2003(2):113-116. |
| [5] | 范景莲,陈玉柏,刘涛,田家敏.纳米晶Mo-Cu复合粉末烧结行为的研究[J].稀有金属材料与工程,2009(10):1693-1697. |
| [6] | Peng Song;Jigui Cheng;Lei Wan .Preparation and characterization of Mo-15 Cu superfine powders by a gelatification-reduction process[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2009(1/2):226-230. |
| [7] | 刘海彦,李增峰,汤慧萍,高广瑞,黄原平.机械合金化制备钼铜复合材料[J].功能材料,2004(z1):3294-3296. |
| [8] | 程继贵,弓艳飞,宋鹏,李洁.凝胶-共还原法制备超细Mo-Cu粉末及其烧结性能[J].中国有色金属学报,2007(03):422-427. |
| [9] | 陈玉柏,范景莲,刘涛,成会朝,田家敏.细晶钼铜合金的制备[J].中国有色金属学报,2008(06):1039-1044. |
| [10] | 胡保全,白培康,程军.Mo-Cu混合粉末机械合金化及固溶度热力学研究[J].中国钨业,2008(06):22-25. |
| [11] | 周贤良,饶有海,华小珍,张建云,邹爱华.机械合金化对Mo-Cu合金性能的影响[J].粉末冶金技术,2007(01):21-23. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%