用溶胶-凝胶法制备了稀土(Ce)掺杂TiO2电极,优化了制备改性TiO2电极的稀土掺杂量、热处理温度及热处理时间. 借助于油田废水化学需氧量(COD)去除情况分析了电极的电催化氧化能力,并分析了电极结构与电催化特性之间的关系. 采用SEM, EDX和XRD分析了制备电极的表面形貌、元素组成和晶体结构. 结果表明,掺杂Ce后电极的表面凹凸感变小,表面更为平滑、致密,几乎没有裂缝,这种均匀一致的高密度小碎片结构可能具有较大的表面粗糙度和比表面积,有利于催化反应. TiO2电极的晶体结构主要为锐钛矿型. 稀土的掺入使得晶相所对应的衍射峰强度变弱且峰形宽化,说明适量Ce的掺杂使涂层表面TiO2晶粒细化了. 在掺杂比为Ti∶Ce=100∶1.5, 热处理温度为450 ℃, 热处理时间为 90 min 时制备的掺杂Ce元素的电极性能最好,此电极对目标有机物COD去除率达到80%, 而不掺杂稀土元素的Ti/TiO2电极为阳极时COD去除率在同样时间内仅为62%, 说明稀土的掺杂提高了电极催化性能.
参考文献
| [1] | Li Y J;Wang F;Zhou G D .[J].Chemosphere,2003,53(10):1229. |
| [2] | Koper MTM .Combining experiment and theory for understanding electrocatalysis[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,2005(2):375-386. |
| [3] | Y.J. Feng;X.Y. Li .Electro-catalytic oxidation of phenol on several metal-oxide electrodes in aqueous solution[J].Water research: A journal of the international water association,2003(10):2399-2407. |
| [4] | 汪文兵,龙晋明,郭忠诚.钛基金属氧化物涂层电极的研究进展[J].电镀与涂饰,2006(07):46-48. |
| [5] | 倪永乐,孟惠民,孙冬柏,俞宏英,樊自拴,王旭东.SbOx+SnO2中间层对Ti/MnO2阳极性能的影响[J].材料科学与工程学报,2007(04):529-532,549. |
| [6] | 王雅琼,王鹏,沙红霞,许文林,陆路德.RuO2含量对Ti/SnO2+Sb2O3/RuO2+PbO2阳极性能的影响[J].稀有金属材料与工程,2007(03):424-427. |
| [7] | 薛彩霞,梁镇海.Ti/SnO2+Sb2O4+CF/PbOx电极的制备及其性能研究[J].太原理工大学学报,2007(05):431-434. |
| [8] | 李善评,胡振,孙一鸣,甄博如,张启磊,曹翰林.新型钛基PbO2电极的制备及电催化性能研究[J].山东大学学报(工学版),2007(03):109-113. |
| [9] | Aal AA;Hassan HB;Rahim MAA .Nanostructured Ni-P-TiO2 composite coatings for electrocatalytic oxidation of small organic molecules[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,2008(0):17-25. |
| [10] | Shibli S M A;Dilimon V S .[J].International Journal of Hydrogen Energy,2008,33(04):1104. |
| [11] | Jari Aromaa;Olof Forsen .Evaluation of the electrochemical activity of a Ti-RuO{sub}2-TiO{sub}2 permanent anode[J].Electrochimica Acta,2006(27):6104-6110. |
| [12] | 孙娟,沈嘉年,姚书典.贵金属掺杂Ti/TiO2电极的制备及其电催化性能研究[J].化学学报,2006(07):647-651. |
| [13] | Zhang WJ;Zhu SL;Li Y;Wang FH .Photocatalytic Zn-doped TiO2 films prepared by DC reactive magnetron sputtering[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,2007(3):328-335. |
| [14] | Wei F Y;Ni L S;Cui P .[J].Journal of Hazardous Materials,2008,156(1-3):135. |
| [15] | 朱蕾,崔晓莉,沈杰,杨锡良,章壮健.直流反应磁控溅射方法制备碳掺杂TiO2薄膜及其可见光活性[J].物理化学学报,2007(11):1662-1666. |
| [16] | 赵宗彦,柳清菊,朱忠其,张瑾.S掺杂对锐钛矿相TiO2电子结构与光催化性能的影响[J].物理学报,2008(06):3760-3768. |
| [17] | Setiawati E;Kawano K .[J].Journal of Alloys and Compounds,2008,451(1-2):293. |
| [18] | 何开棘,张圣军,丁慧,王开明.掺铁纳米TiO2粉体的制备及其光催化活性的研究[J].鞍山科技大学学报,2007(05):449-452. |
| [19] | 张翼,刘蕾,孙晓东,张荣庆,王磊.Fe掺杂钛基SnO2/Sb电催化电极的制备及表征[J].材料保护,2008(03):31-33,70. |
| [20] | 张翼,王磊,闫红娟,司文彬.钕掺杂Ti基Sn-Sb涂层电极的制备及性能评价[J].中国稀土学报,2007(06):760-764. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%